Covestro Bayblend? FR3010 HF PC/ABS Blend
Polymer,Thermoplastic,ABS Polymer,Polycarbonate/ABS Alloy, Unreinforced,Polycarbonate (PC)
Covestro
产品说明:
Main characteristics:
? High toughness even at low temperatures
? High dimensional accuracy and stability
? Good paintability
? Good flowability
Grade characteristics:
? Flame-retardant
? Injection molding
? Easy flow
As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Covestro Bayblend? FR3010 HF PC/ABS Blend 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183-1 |
| 平衡吸湿 | 0.20 % | 0.20 % | ISO 62, 50% RH |
| 饱和吸水率 | 0.50 % | 0.50 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.118 in |
150x105x3mm; b.o. ISO 2577 |
| 线性成型收缩率，横向 | 0.0050 - 0.0070 cm/cm @Thickness 3.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.118 in |
150x105x3mm; b.o. ISO 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-1,-2 |
| 抗张强度(屈服) | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-1,-2 |
| 伸长率 (断裂) | >= 50 % | >= 50 % | 50 mm/min; b.o. ISO 527-1,-2 |
| 屈服伸长率 | 4.0 % | 4.0 % | 50 mm/min; ISO 527-1,-2 |
| 拉伸模量 | 2.70 GPa | 392 ksi | 1 mm/min; ISO 527-1,-2 |
| 悬壁梁缺口冲击强度 | 10.0 kJ/m2 @Temperature -30.0 °C |
4.76 ft-lb/in2 @Temperature -22.0 °F |
ISO 180-A |
| 35.0 kJ/m2 @Temperature 23.0 °C |
16.7 ft-lb/in2 @Temperature 73.4 °F |
ISO 180-A | |
| 悬壁梁无缺口冲击强度 | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180-U |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| 表面电阻 | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| 介电常数 | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
IEC 60250 | |
| 介电强度 | 30.0 kV/mm @Thickness 1.00 mm |
762 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| 耗散因数 | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
IEC 60250 |
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | 350 V | 350 V | Solution A; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 76.0 μm/m-°C @Temperature 23.0 - 55.0 °C |
42.2 μin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| 线性热膨胀系数,横向流动 | 80.0 μm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 μin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| 载荷下热变形温度(0.46 MPa) | 100 °C | 212 °F | ISO 75-1,-2 |
| 载荷下热变形温度(1.8 MPa) | 90.0 °C | 194 °F | ISO 75-1,-2 |
| 维卡软化温度 | 106 °C @Load 5.10 kg |
223 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 108 °C @Load 5.10 kg |
226 °F @Load 11.2 lb |
120°C/h; ISO 306 | |
| 可燃性(UL94) | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VB @Thickness 2.20 mm |
5VB @Thickness 0.0866 in |
UL 94-5V | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94-5V |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 240 °C | 464 °F | Injection molding; ISO 294 |
| 模具温度 | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| 射速 | 240 mm/sec | 9.45 in/sec | ISO 294 |