无锡市韵鸿塑化有限公司
PMMA(聚甲基丙烯酸甲酯#有机玻璃|压克力)/CP-81/路彩特(台湾/镇江)
用途:眼镜支撑片、电子、挤出棒和管、反光镜、放大镜、微波炉门、寻呼机和手机屏、钢琴键盘、路灯罩
特性备注:干燥条件:70-85℃模具温度:70-90℃料售温度:180-230℃注塑压力:700-1400kg/cm2退火条件2-4小时:65-80℃
重要参数:熔体流动速率:1.8 g/10min密度:1.19 g/cm3吸水率:0.3 %成型收缩率:0.004 %缺口冲击强度:0.4 拉伸强度:67 MPa弯曲强度:108 MPa弯曲模量:2923 MPa硬度:95 维卡软化点:107 ℃热变形温度:98 ℃透光率:92 %
PMMA/路彩特(台湾)/CP-81A物性表
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 熔体流动速率 | --- | ASTM D-1238 | 1.8 | g/10min |
吸水性 | --- | ASTM D-570 | 0.3 | % | |
物理性能 | 模具收缩率 | --- | ASTM D-955 | 0.002-0.006 | --- |
比重 | --- | ASTM D-792 | 1.19 | --- | |
透光率 | --- | ASTM D-1003 | 92 | % | |
折射率 | --- | ASTM D-542 | 1.49 | --- | |
机械性能 | 拉伸强度 | --- | ASTM D-638 | 9800 | Psi |
延伸率 | --- | ASTM D-638 | 4.0 | % | |
挠曲模量 | --- | ASTM D-790 | 424000 | Psi | |
洛氏硬度 | --- | ASTM D-785 | 95 | M SCALE | |
挠曲强度 | --- | ASTM D-790 | 15700 | Psi | |
IZOD缺口冲击强度 | --- | ASTM D-256 | 0.4 | --- | |
热 性 能 | 可燃性 | --- | UL 94 | HB | --- |
热变形温度 | --- | ASTM D-648 | 98 | ℃ | |
维卡软化点 | --- | ASTM D-1525 | 107 | ℃ |