上海霄鸿实业有限公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-792 | 1.56 | ||
| 物理性能 | 吸水量 | 24hrs浸泡 73?H( 23℃) | ASTM D-570 | 0.25 | % |
| 吸水量 | Equil.50%R.h. 73?H( 23℃) | ASTM D-570 | 0.20 | % | |
| 吸水量 | 浸泡均衡点 73?H( 23℃) | ASTM D-570 | 1.00 | % | |
| 机械性能 | 挠曲系数 | 212?H | 在25℃下 | 300 | MPsi |
| 压缩应力 | 73?H@10%ASTM D-ef. | ASTM D-695 | 18.0 | MPsi | |
| 伸张强度 | 23℃ | ASTM D-638 | 58.6 | MPa | |
| 弯曲疲劳忍耐限度 | 73?H | ASTM D-671 | 4.5 | MPsi | |
| 洛氏硬度 | ASTM D-785 | M90,R118 | |||
| 挠曲系数 | 70℃ | 在25℃下 | 3795 | MPa | |
| 挠曲系数 | 250?H | 在25℃下 | 270 | MPsi | |
| 伸张强度 | 122℃ | ASTM D-638 | 20.7 | MPa | |
| 断裂时之拉力伸张度 | 73?H( 23℃) | ASTM D-638 | 12 | % | |
| 负载下之变形 | 2000psi@ 122?H(14Mpa@50℃) | ASTM D-621 | 0.4 | % | |
| 挠曲系数 | 100℃ | 在25℃下 | 2480 | MPa | |
| 挠曲系数 | 23℃ | 在25℃下 | 5030 | MPa | |
| 弯曲降服强度 | 73?H | ASTM D-790 | 10.7 | MPsi | |
| 剪力 | 23℃ | ASTM D-732 | 65.5 | MPa | |
| 挠曲系数 | 122℃ | 在25℃下 | 1860 | MPa | |
| 拉力冲击抵抗力 | 73?H | ASTM D-1822 | 33 | ft.lb/in2 | |
| 弹性系数 | 23℃ | ASTM D-638 | 6200 | MPa | |
| 伸张强度 | -55℃ | ASTM D-638 | 88.0 | MPa | |
| 伸张强度 | 212?H | ASTM D-638 | 4.1 | MPsi | |
| 伸张强度 | 250?H | ASTM D-638 | 3.0 | MPsi | |
| 压缩应力 | 73?H@1%ASTM D-ef. | ASTM D-695 | 5.2 | MPsi | |
| 挠曲系数 | 73?H | 在25℃下 | 730 | MPsi | |
| 断裂时之拉力伸张度 | 212?H( 100℃) | ASTM D-638 | >260 | % | |
| 拉力冲击抵抗力 | 23℃ | ASTM D-1822 | 67 | kj/m2 | |
| 剪力 | 73?H | ASTM D-732 | 9.5 | MPsi | |
| 伸张强度 | -68?H | ASTM D-638 | 12.7 | MPsi | |
| 断裂时之拉力伸张度 | 158?H( 70℃) | ASTM D-638 | 50 | % | |
| 摩擦系数 | 73?H( 23℃)动态 | ThrustWasherTest3 | 0.35 | ||
| 绝缘强度 | Short Time,2.3mm | 19.3(3.2mm) | MV/m | ||
| 弹性系数 | 73?H | ASTM D-638 | 900 | MPsi | |
| 伸张强度 | 158?H | ASTM D-638 | 5.8 | MPsi | |
| 断裂时之拉力伸张度 | -68?H(-55℃) | ASTM D-638 | 3 | % | |
| 挠曲系数 | -68?H | 在25℃下 | 930 | MPsi | |
| IZOD冲击强度 | -40?H | ASTM D-256 | 0.5 | ft.lb/in | |
| 挠曲系数 | 158?H | 在25℃下 | 550 | MPsi | |
| 挠曲系数 | -55℃ | 在25℃下 | 6410 | MPa | |
| 伸张强度 | 70℃ | ASTM D-638 | 40.0 | MPa | |
| IZOD冲击强度 | 23℃ | ASTM D-256 | 42.7 | j/m | |
| 伸张强度 | 73?H | ASTM D-638 | 8.5 | MPsi | |
| 压缩应力 | 23℃@1%ASTM D-ef. | ASTM D-695 | 36.0 | MPa | |
| IZOD冲击强度 | 40℃ | ASTM D-256 | 26.7 | j/m | |
| 压缩应力 | 23℃@10%ASTM D-ef. | ASTM D-695 | 124 | MPa | |
| 伸张强度 | 100℃ | ASTM D-638 | 28.3 | MPa | |
| 弯曲降服强度 | 23℃ | ASTM D-790 | 73.8 | MPa | |
| 断裂时之拉力伸张度 | 250?H( 122℃) | ASTM D-638 | >260 | % | |
| IZOD冲击强度 | 73?H | ASTM D-256 | 0.8 | ft.lb/in | |
| 扩散因数 | 73?H( 23℃)106Hz | ASTM D-150 | 0.005 | ||
| 弯曲疲劳忍耐限度 | 23℃ | ASTM D-671 | 31.0 | MPa | |
| 绝缘强度 | Short Time,90 mils | ASTM D-149 | 490(125mils) | V/mil | |
| 电气性能 | 电阻系数 | 73?H( 23℃)0.2%H2O | ASTM D-257 | 5×1014 | ohm-cm |
| 电弧抵抗力 | 120mil(3.1mm) | ASTM D-495 | 168no tracking | Sec. | |
| 绝缘系数 | 73°F( 23℃)102to106Hz | ASTM D-150 | 3.9 | ||
| 热性能 | 线性热膨胀系数 | -40 to 85?H | ASTM D-696 | 2.0-4.5 | 10-5in/in.°F |
| 热变形温度 | 0.5MPa | ASTM D-648 | 174 | ℃ | |
| 热变形温度 | 66psi | ASTM D-648 | 345 | ?H | |
| 熔点 | ASTM D-2133 | 175 | ℃ | ||
| 热变形温度 | 1.8MPa | ASTM D-648 | 158 | ℃ | |
| 可燃烧性 | UL-94 | 94HB | |||
| 熔点 | ASTM D-2133 | 347 | ?H | ||
| 热变形温度 | 264psi | ASTM D-648 | 316 | ?H | |
| 线性热膨胀系数 | -40 to 29℃ | ASTM D-696 | 3.6-8.1 | 10-5m/m.℃ | |