上海霄鸿实业有限公司
原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D792 | 0.91 | g/cm3 | |
| 熔体流动速率 | 230℃，2.16kg | ASTM D-1238 | 0.2 | g/10min | |
| 熔体流动速率 | 190℃，5.0kg | ASTM D-1238 | 0.4 | g/10min | |
| 机械性能 | 抗张力 | 破断点 | ASTM D-638 | 230 | kg/cm2 |
| IZOD冲击强度 | 23℃ | ASTM D-256 | No break | kg·cm/cm | |
| 弯曲弹性率 | ASTM D-790 | 8,500 | kg/cm2 | ||
| IZOD冲击强度 | -20℃ | ASTM D-256 | 3 | kg·cm/cm | |
| 伸长率 | ASTM D-638 | ＞400 | % | ||
| 抗张力 | 降伏点 | ASTM D-638 | 270 | kg/cm2 | |
| 表面抵抗 | HS Method | ＞1013 | Ω | ||
| IZOD冲击强度 | 0℃ | ASTM D-256 | 8 | kg·cm/cm | |
| 热性能 | 线膨胀系数 | 0-110℃ | Dilatometer | 1.5×10-4 | K-1 |
| 维卡软化点 | ASTM D-1525 | 130 | ℃ | ||
| 熔点 | HS Method | 141 | ℃ | ||