东莞市恒磊塑胶有限公司
Lupoy? GN2101F
Technical Datasheet | Supplied by LG Chem
Lupoy? GN2101F is a halogen-free flame retardant polycarbonate grade by LG Chem, reinforced with 10% glass fiber. Exhibits high performance and high heat resistance. Lupoy? GN2101F is suitable for processing by injection molding. Used in IT/OA, electrical & electronic housings and components. Complies with UL 94 V-0 and 5VA flame rating.
| 加工/物理特性 | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ASTM数据(ASTM Data) | |||
| 熔体流动指数(Melt Flow Index) | 11 | g/10min | ASTM D 1238 |
| 温度(Temperature) | 300 | °C | - |
| 负载(Load) | 1.2 | kg | - |
| 模具收缩(Mold Shrinkage) (MD) | 0.003 | mm/mm | ASTM D 955 |
| 密度(Density) (73°F) | 1250 | kg/m3 | ASTM D 792 |
| 机械性能(机械性能(Mechanical properties)) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) |
| ASTM数据(ASTM Data) | |||
| 抗拉强度(Tensile Strength) at Yield | 76.5 | MPa | ASTM D 638 |
| 断裂伸长率(Elongation at Break) | 10 | % | ASTM D 638 |
| 弯曲弹性模量(弯曲弹性模量(Flexural Modulus)) | 3825.9 | MPa | ASTM D 790 |
| 抗弯强度(Flexural Strength) | 123 | MPa | ASTM D 790 |
| 洛氏硬度(Rockwell Hardness) | R 124 | - | ASTM D 785 |
| 悬臂梁式冲击无切口(Izod Impact unnotched) (1/8 in) | 0.0754 | kJ/m | ASTM D 256 |
PC LUPOY GN2101F
塑料的处理
PC塑胶原料的吸水率较大，加工前一定要预热干燥，纯PC干燥120℃，改性PC一般用110℃温度干燥4小时以上。干燥时间不能超过10小时。一般可用对空挤出法判断干燥是否足够。再生料的使用比例可达20%。在某些情况下，可100%的使用再生料，实际份量要视制品的品质要求而定。再生料不能同时混合不同的色母粒，否则会严重损坏成品的性质。
注塑机选用
PC塑料制品由于成本及其它方面的原因，多用改性材料，特别是电工产品，还须增加防火性能，在阻燃的PC和其它塑料合金产品成型时，对注塑机塑化系统的要求是混合好、耐腐蚀，常规的塑化螺杆难以做到，在选购时，一定要预先说明。
主要优点
1．具高强度及弹性系数、高冲击强度、使用温度范围广；
2．高度透明性及自由染色性；
3．成形收缩率低、尺寸安定性良好；
4．耐疲劳性佳；
5．耐候性佳；
6．电气特性优。
性能特点:良好的流动性;脱模性能良好;
粘度，高；光学透明性好、抗冲击强度高；
并具有优异的热安稳性、耐蠕变性、抗寒性、电绝缘性和阻燃性等。
加工方法:薄膜挤出；吹塑成型；挤出成型；热成型；树脂传递成型；涂层；砑光；注射成型也是最重要的加工方法之一；
用途:在透明建筑板材、电子电器、光盘、汽车工业、机械、光学、医药等领域得到广泛运用。
PC塑料物理性能以及加工
低温-45度聚碳酸酯无色透明，耐热，抗冲击，阻燃BI级，在普通运用温度内都有出色的机械功用。