ABS TERLURAN HI-12

Terluran HI-12 is an injection molding grade of ABS with a very high toughness and easy flow.

• Very high toughness

• Easy flowing

• UL 94 HB (1.6 & 3.2 mm)

  Information provided by Styrolution

Physical Properties	Metric	English	Comments
Density	1.02 g/cc	0.0368 lb/in3	ISO 1183
Moisture Absorption at Equilibrium	0.21 % @Temperature 23.0 °C	0.21 % @Temperature 73.4 °F	50% RH; ISO 62
Water Absorption at Saturation	1.03 % @Temperature 23.0 °C	1.03 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ISO 294-4
Melt Flow	14 g/10 min @Load 10.0 kg, Temperature 220 °C	14 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	101	101	IEC 2039-2
Ball Indentation Hardness	80.0 MPa	11600 psi	ISO 2039-1
Tensile Strength, Yield	40.0 MPa	5800 psi	ISO 527
Elongation at Yield	2.7 %	2.7 %	ISO 527
Tensile Modulus	1.90 GPa	276 ksi	ISO 527
Flexural Strength	58.0 MPa	8410 psi	ISO 178
Izod Impact, Notched (ISO)	11.0 kJ/m2 @Temperature -30.0 °C	5.23 ft-lb/in2 @Temperature -22.0 °F	ISO 180/A

ABS TERLURAN HI-12 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！

ABS是一种综合性能十分良好的树脂，在比较宽广的温度范围内具有较高的冲击强度和表面硬度，热变形温度比PA、PVC高，尺寸稳定性好。

一般性能 ：

ABS的外观为不透明呈象牙色的粒料，无毒、无味、吸水率低其制品可着成各种颜色，并具有90%的高光泽度。ABS同其它材料的结合性好，易于表面印刷、涂层和镀层处理。ABS的氧指数为18.2，属易燃聚合物，火焰呈黄色，有黑烟，烧焦但不滴落，并发出特殊的肉桂味。

（1）力学性能

ABS有优良的力学性能，其冲击强度较好，可以在极低的温度下使用。即使ABS制品被破坏，也只能是拉伸破坏而不会是冲击破坏。ABS的耐磨性能优良，尺寸稳定性好，又具有耐油性，可用于中等载荷和转速下的轴承。ABS的蠕变性比PSF及PC大，但比PA和POM小。ABS的弯曲强度和压缩强度属塑料中较差的。ABS的力学性能受温度的影响较大。

（2）热学性能

ABS属于无定形聚合物，无明显熔点；熔体粘度较高，流动性差，耐候性较差，紫外线可使变色；热变形温度为70—107℃（85左右），制品经退火处理后还可提高10℃左右。对温度，剪切速率都比较敏感；ABS在－40℃时仍能表现出一定的韧性，可在 -40℃到85℃的温度范围内长期使用。

应用：

1、汽车产业

汽车产业中有众多零件是用ABS或ABS合金制造的，如上海的桑塔纳轿车，每辆车用ABS11kg，位列汽车中所用塑料第三。在其它车辆中，ABS的使用量也颇惊人。2000年我国就汽车用ABS的量就达到3.5万吨。轿车中主要零部件使用ABS的如仪表板用PC/ABS作骨架，表面再复以PVC/ABS/BOVC制成的薄膜。此外，车内装饰件大量使用了ABS，如手套箱、杂物箱总成是用耐热ABS制成，门槛上下饰件、水箱面罩用ABS制成，另外还有很多零件采用ABS为原料。