ABS TERLURAN GP-25

Terluran GP-25 is an easy-flow, general purpose injection molding grade with high resistance to impact and heat distortion; intended for a wide range of applications, particularly in the housings sector.

• Excellent colorability

• Medium flow

• Good impact resistance

• Good heat distortion resistance

• High quality surface finish and gloss

Information provided by Styrolution

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in3	ISO 1183
Moisture Absorption at Equilibrium	0.21 % @Temperature 23.0 °C	0.21 % @Temperature 73.4 °F	50% RH; ISO 62
Water Absorption at Saturation	0.95 % @Temperature 23.0 °C	0.95 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ISO 294-4
Melt Flow	25 g/10 min @Load 10.0 kg, Temperature 220 °C	25 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	99.0 MPa	14400 psi	ISO 2039-1
Tensile Strength, Yield	44.0 MPa	6380 psi	ISO 527
Elongation at Break	12 %	12 %	ISO 527
Elongation at Yield	2.4 %	2.4 %	ISO 527
Tensile Modulus	2.30 GPa	334 ksi	ISO 527
Flexural Strength	65.0 MPa	9430 psi	ISO 178
Izod Impact, Notched (ISO)	7.00 kJ/m2 @Temperature -30.0 °C	3.33 ft-lb/in2 @Temperature -22.0 °F	ISO 180/A

ABS TERLURAN GP-25

成型性能

无定形材料,流动性中等,吸湿大,必须充分干燥,表面要求光泽的塑件须长时间预热干燥80-90度,3小时；

宜取高料温,高模温,但料温过高易分解(分解温度为>270度).对精度较高的塑件,模温宜取50-60度,对高光泽.耐热塑件,模温宜取60-80度；

如需解决夹水纹，需提高材料的流动性，采取高料温、高模温，或者改变入水位等方法；

如成形耐热级或阻燃级材料，生产3-7天后模具表面会残存塑料分解物，导致模具表面发亮，需对模具及时进行清理，同时模具表面需增加排气位置；

冷却速度快，模具浇注系统应以粗，短为原则，宜设冷料穴，浇口宜取大，如：直接浇口，圆盘浇口或扇形浇口等，但应防止内应力增大，必要时可采用调整式浇口。模具宜加热，应选用耐磨钢； 

料温对塑件质量影响较大，料温过低会造成缺料，表面无光泽，银丝紊乱料温过高易溢边，出现银丝暗条，塑件变色起泡；

用途

ABS树脂的最大应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。

ABS TERLURAN GP-25 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！