POM CELCON MC90-HM

Celcon? MC90-HM is a highly mineral filled and coupled M90 material for producing very flat and dimensionally stable parts (normal flow).

Information provided by Celanese

Physical Properties	Metric	English	Comments
Specific Gravity	1.60 g/cc	1.60 g/cc	ASTM D792
Density	1.57 g/cc	0.0567 lb/in3	ISO 1183
Moisture Absorption	0.200 %	0.200 %	23°C/50%RH; ISO 62
Water Absorption at Saturation	0.75 %	0.75 %	ISO 62
Linear Mold Shrinkage, Flow	0.015 cm/cm	0.015 in/in	ISO 294-4
	0.015 cm/cm	0.015 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.012 cm/cm	0.012 in/in	ASTM D955
	0.013 cm/cm	0.013 in/in	ISO 294-4
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	44.1 MPa	6400 psi	ASTM D638
	45.0 MPa	6530 psi	50mm/min; ISO 527-2/1A
Elongation at Yield	6.0 %	6.0 %	50mm/min; ISO 527-2/1A
Tensile Modulus	3.55 GPa	515 ksi	50mm/min; ISO 527-2/1A
Flexural Strength	72.0 MPa	10400 psi	ISO 178
Flexural Modulus	3.45 GPa	500 ksi	ASTM D790
	3.50 GPa	508 ksi	ISO 178
Izod Impact, Notched	0.641 J/cm	1.20 ft-lb/in	ASTM D256
Izod Impact, Notched (ISO)	6.10 kJ/m2	2.90 ft-lb/in2	ISO 180/1A

POM CELCON MC90-HM

特点

（1）POM加工前可不用干燥,最好在加工过程中进行预热(80℃左右),对产品尺寸的稳定性有好处.

　　（2） POM的加工温度很窄(0～215℃),在炮筒内停留时间稍长或温度超过220℃时就会分解,产生刺激性强的甲醛气体.

　　（3） POM料注塑时保压压力要较大(与注射压力相近),以减少压力降.螺杆转速不能过高,残量要少;

　　（4） POM产品收缩率较大,易产生缩水或变形.POM比热大,模温高(80～100℃),产品脱模时很烫,需防止烫伤手指.

　　（5） POM宜在“中压、中速、低料温、较高模温”的条件下成型加工,精密制品成型时需用控制模温

　　（6）具高机械强度和刚性

　　（7）最高的疲劳强度

　　（8）环境抵抗性、耐有机溶剂性佳

　　（9）耐反覆冲击性强,良好的电气性质,复原性良好,具自已润滑性、耐磨性良好,尺寸安定性优.

应用

.可代替大部分有色金属、汽车、机床、仪表内件、轴承、紧固件、齿轮、弹簧片、管道、运输带配件、电水煲、泵壳、沥水器、水龙头等.

POM CELCON MC90-HM 我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！