EXL1494T NA8A005T

LEXAN Copolymer EXL1494T - Asia

聚碳酸酯

SABIC

Product Description:

LEXAN EXL1494T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance. This resin offers extreme low temperature (-40 C) ductility in combination with medium flow characteristics, improved release and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1494T resin is available in transparent and opaque colors and is an excellent candidate for a broad range of food contact applications.

• 
  

总览
材料状态	已商用：当前有效
UL 黄卡 1	E207780-466358
搜索 UL 黄卡	SABIC
供货地区	亚太地区
用途	电气/电子应用领域电器用具电子显示器非特定食品应用药物
Also Available In	EuropeLatin AmericaNorth America

物理性能	额定值	单位制	测试方法
密度 / 比重	1.19	g/cm3	ASTM D792, ISO 1183
熔流率（熔体流动速率） (300°C/1.2 kg)	10	g/10 min	ASTM D1238
熔融体积流量（MVR） (300°C/1.2 kg)	9.0	cm3/10min	ISO 1133
收缩率			内部方法
垂直 : 3.20 mm	0.40 到 0.80	%
流动 : 3.20 mm	0.40 到 0.80	%
吸水率			ISO 62
饱和, 23°C	0.12	%
平衡, 23°C, 50% RH	0.090	%
硬度	额定值	单位制	测试方法
洛氏硬度 (L 计秤)	87		ASTM D785

机械性能	额定值	单位制	测试方法
拉伸模量
-- 2	2180	MPa	ASTM D638
--	2300	MPa	ISO 527-2/1
抗张强度
屈服 3	57.0	MPa	ASTM D638
屈服	56.0	MPa	ISO 527-2/50
断裂 3	59.0	MPa	ASTM D638
断裂	55.0	MPa	ISO 527-2/50
伸长率
屈服 3	5.6	%	ASTM D638
屈服	5.4	%	ISO 527-2/50
断裂 3	120	%	ASTM D638
断裂	110	%	ISO 527-2/50
弯曲模量
50.0 mm 跨距 4	2180	MPa	ASTM D790
-- 5	2120	MPa	ISO 178
弯曲应力
-- 5, 6	88.0	MPa	ISO 178
屈服, 50.0 mm 跨距 4	92.0	MPa	ASTM D790