Hostaform? C 9021 K
聚甲醛（POM）共聚物
白垩填料
产品说明：
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 03-002, K5
POM copolymer
Injection molding type, with special chalk modified; good wear
properties; good chemical resistance to solvents, fuel and strong
alkalis as well as good hydrolysis resistance; high resistance to
thermal and oxidative degradation.
UL-registration in natural and a thickness more than 1.57 mm as UL 94
HB, temperature index UL 746 B electrical 105°C, mechanical 90°C
(tensile impact) and 80°C (tensile).
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness
more than 1 mm.
Ranges of applications: for unlubricated or once-only-lubricant
sliding Parts.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)
Hostaform? C 9021 K 物性表
| 基本信息 |
|
| |
|
| 填料/增强材料 |
|
| 特性 |
|
| RoHS 合规性 |
|
| 加工方法 |
|
| 多点数据 |
Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) |
| 树脂ID (ISO 1043) |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 密度 |
1.44 |
g/cm3 |
ISO 1183 |
| 溶化体积流率（MVR） (190°C/2.16 kg) |
7.50 |
cm3/10min |
ISO 1133 |
| 收缩率 |
|
|
ISO 294-4 |
| 垂直流动方向 |
1.8 |
% |
ISO 294-4 |
| 流动方向 |
2.0 |
% |
ISO 294-4 |
| 吸水率 (饱和, 23°C) |
0.65 |
% |
ISO 62 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
3000 |
MPa |
ISO 527-2/1A/1 |
| 拉伸应力 (屈服) |
60.0 |
MPa |
ISO 527-2/1A/50 |
| 拉伸应变 (屈服) |
8.0 |
% |
ISO 527-2/1A/50 |
| 标称拉伸断裂应变 |
22 |
% |
ISO 527-2/1A/50 |
| 拉伸蠕变模量 |
|
|
ISO 899-1 |
| 1 hr |
2500 |
MPa |
ISO 899-1 |
| 1000 hr |
1400 |
MPa |
ISO 899-1 |
| 弯曲模量 (23°C) |
2900 |
MPa |
ISO 178 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
ISO 179/1eA |
| -30°C |
5.0 |
kJ/m2 |
ISO 179/1eA |
| 23°C |
5.0 |
kJ/m2 |
ISO 179/1eA |
| 简支梁无缺口冲击强度 |
|
|
ISO 179/1eU |
| -30°C |
100 |
kJ/m2 |
ISO 179/1eU |
| 23°C |
100 |
kJ/m2 |
ISO 179/1eU |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 热变形温度 (1.8 MPa, 未退火) |
100 |
°C |
ISO 75-2/A |
| 熔融温度 1 |
166 |
°C |
ISO 11357-3 |
| 线形热膨胀系数 - 流动 |
1.1E-4 |
cm/cm/°C |
ISO 11359-2 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+14 |
ohms |
IEC 60093 |
| 体积电阻率 |
1.0E+14 |
ohms·cm |
IEC 60093 |
| 介电强度 |
35 |
kV/mm |
IEC 60243-1 |
| 相对电容率 |
|
|
IEC 60250 |
| 100 Hz |
4.20 |
|
IEC 60250 |
| 1 MHz |
4.20 |
|
IEC 60250 |
| 耗散因数 |
|
|
IEC 60250 |
| 100 Hz |
2.5E-3 |
|
IEC 60250 |
| 1 MHz |
6.0E-3 |
|
IEC 60250 |
| 漏电起痕指数 |
600 |
V |
IEC 60112 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 1.57 mm |
HB |
|
UL 94 |
| 3.18 mm |
HB |
|
UL 94 |
| 充模分析 |
额定值 |
单位制 |
测试方法 |
| Density of Melt |
1.230 |
g/cm3 |
内部方法 |
| Ejection Temperature |
164 |
°C |
内部方法 |
| Specific Heat Capacity of Melt |
2060 |
J/kg/°C |
内部方法 |
| Thermal Conductivity of Melt |
0.20 |
W/m/K |
内部方法 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
100 到 120 |
°C |
|
| 干燥时间 |
3.0 到 4.0 |
hr |
|
| 建议的最大水分含量 |
0.15 |
% |
|
| 料斗温度 |
20.0 到 30.0 |
°C |
|
| 料筒后部温度 |
170 到 180 |
°C |
|
| 料筒中部温度 |
180 到 190 |
°C |
|
| 料筒前部温度 |
190 到 200 |
°C |
|
| 射嘴温度 |
190 到 210 |
°C |
|
| 加工（熔体）温度 |
190 到 210 |
°C |
|
| 模具温度 |
80.0 到 120 |
°C |
|
| 注塑压力 |
60.0 到 120 |
MPa |
|
| 注射速度 |
慢 |
|
|
| 保压 |
60.0 到 120 |
MPa |
|
| 背压 |
0.00 到 2.00 |
MPa |
|
| 注射说明 |
| Manifold Temperature: 190 to 210°CZone 4 Temperature: 190 to 210°CFeed Temperature: 60 to 80°C |