TOYOLAC? 300-325
Technical Datasheet | Supplied by Toray
TOYOLAC 300-325 is a standard acrylonitrile butadiene styrene (ABS) grade. Is an electrically insulating material. Exhibits super high rigidity. Shows high strength and is very light and aesthetic. Possesses heat stability, excellent mechanical- , chemical- and electrical properties and superior processability. Can be processed using injection molding. Recommended for housing equipment applications. Complies with UL 94 HB Flame Rating.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.04 | g/cm3 | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (220°C/10.0 kg) | 15 | g/10 min | ISO 1133 |
| 收缩率 - 流动 | 0.40 到 0.60 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 级) | 107 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 2500 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 1 | 43.0 | MPa | ASTM D638 |
| 屈服 | 47.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 断裂 2 | 20 | % | ASTM D638 |
| 断裂 | > 10 | % | ISO 527-2/50 |
| 弯曲模量 3 | 2250 | MPa | ASTM D790 |
| 弯曲强度 | |||
| -- 4 | 66.0 | MPa | ASTM D790 |
| -- 5 | 69.0 | MPa | ISO 178 |
1）一般性能 ：
ABS的外观为不透明呈象牙色的粒料，无毒、无味、吸水率低其制品可着成各种颜色，并具有90%的高光泽度。ABS同其它材料的结合性好，易于表面印刷、涂层和镀层处理。ABS的氧指数为18.2，属易燃聚合物，火焰呈黄色，有黑烟，烧焦但不滴落，并发出特殊的肉桂味。
ABS是一种综合性能十分良好的树脂，在比较宽广的温度范围内具有较高的冲击强度和表面硬度，热变形温度比PA、PVC高，尺寸稳定性好。
（1）力学性能
ABS有优良的力学性能，其冲击强度较好，可以在极低的温度下使用。即使ABS制品被破坏，也只能是拉伸破坏而不会是冲击破坏。ABS的耐磨性能优良，尺寸稳定性好，又具有耐油性，可用于中等载荷和转速下的轴承。ABS的蠕变性比PSF及PC大，但比PA和POM小。ABS的弯曲强度和压缩强度属塑料中较差的。ABS的力学性能受温度的影响较大。
（2）热学性能
ABS属于无定形聚合物，无明显熔点；熔体粘度较高，流动性差，耐候性较差，紫外线可使变色；热变形温度为70—107℃（85左右），制品经退火处理后还可提高10℃左右。对温度，剪切速率都比较敏感；ABS在－40℃时仍能表现出一定的韧性，可在 -40℃到85℃的温度范围内长期使用。