余姚市利和塑化有限公司
原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 流动性 | ASTM D1238 | 10 | g/10min | ||
| 密度 | ASTM D792 | 1.2 | ||||
| 模塑收缩率 | ASTM D955 | 0.5-0.7 | % | |||
| 吸水率 | ASTM D570 | 0.2 | % | |||
| 机械性能 | 拉伸强度 | ASTM D638 | 630 | kg/cm2 | ||
| 伸长率 | ASTM D638 | 110 | % | |||
| 弯曲强度 | ASTM D790 | 920 | kg/cm2 | |||
| 弯曲模量 | ASTM D790 | 24000 | kg/cm2 | |||
| 洛氏硬度 | ASTM D785 | 77 | M | |||
| 缺口冲击强度 | ASTM D256 | 87 | kg.cm/cm | |||
| 电气性能 | 体积电阻率 | 1016 | ASTM D257 | 3 | Ω.cm | |
| 损耗因数 | ASTM D150 | 2.95 | ||||
| 热性能 | 热变形温度 | - | 1.8Mpa | ASTM D648 | 125 | ℃ |
| - | 0.45Mpa | ASTM D648 | 136 | ℃ | ||
| 线膨胀系数 | ASTM D696 | 6-8 | ||||
| 维卡软化温度 | ASTM D1525 | 153 | ℃ | |||
| 光学性能 | 透光率 | ASTM D1003 | 89 | % | ||
| 雾度 | ASTM D1003 | ＜0.8 | % | |||
| 折射率 | ASTM D542 | 1.585 | ||||