ABS Lustran 349

Lustran? 349 is a high-gloss, medium-impact injection molding resin that has been specially formulated for excellent surface lubricity using internal additives. Healthcare certifications, High gloss, Medium impact, Excellent surface lubricity, UL 94 HB rated. Applications: Components of intravenous (IV)systems, Surgical instruments, Diagnostic test kits

Information provided by Styrolution.

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in3	ASTM D 792
Linear Mold Shrinkage	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	ASTM D 955
Melt Flow	6.0 g/10 min @Load 3.80 kg, Temperature 230 °C	6.0 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D 1238
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	110	110	ASTM D 785
Tensile Strength, Yield	42.1 MPa	6110 psi	ASTM D 638
Tensile Modulus	2.62 GPa	380 ksi	ASTM D 638
Flexural Strength	72.4 MPa	10500 psi	ASTM D 790
Flexural Modulus	2.69 GPa	390 ksi	ASTM D 790
Izod Impact, Notched	2.67 J/cm @Temperature 23.0 °C	5.00 ft-lb/in @Temperature 73.4 °F	ASTM D 256
Thermal Properties	Metric	English	Comments
CTE, linear	81.0 μm/m-°C	45.0 μin/in-°F	ASTM D 696
Deflection Temperature at 1.8 MPa (264 psi)	87.8 °C	190 °F	unannealed; ASTM D 648
Vicat Softening Point	104 °C @Load 1.02 kg	219 °F @Load 2.25 lb	B/2 120C/H; ASTM D 1525

ABS Lustran 349

成型性能

无定形材料,流动性中等,吸湿大,必须充分干燥,表面要求光泽的塑件须长时间预热干燥80-90度,3小时；

宜取高料温,高模温,但料温过高易分解(分解温度为>270度).对精度较高的塑件,模温宜取50-60度,对高光泽.耐热塑件,模温宜取60-80度；

如需解决夹水纹，需提高材料的流动性，采取高料温、高模温，或者改变入水位等方法；

如成形耐热级或阻燃级材料，生产3-7天后模具表面会残存塑料分解物，导致模具表面发亮，需对模具及时进行清理，同时模具表面需增加排气位置；

冷却速度快，模具浇注系统应以粗，短为原则，宜设冷料穴，浇口宜取大，如：直接浇口，圆盘浇口或扇形浇口等，但应防止内应力增大，必要时可采用调整式浇口。模具宜加热，应选用耐磨钢； 

料温对塑件质量影响较大，料温过低会造成缺料，表面无光泽，银丝紊乱料温过高易溢边，出现银丝暗条，塑件变色起泡；

用途

ABS树脂的最大应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。