Technical Datasheet | Supplied by LG Chem
Lupoy? GP5100 is a general purpose polycarbonate and acrylonitrile butadiene styrene (PC/ ABS) alloy by LG Chem, reinforced with 10% glass fiber. Exhibits high performance and dimensional stability. Lupoy? GP5100 is suitable for processing by injection molding. Used in electrical appliance housings and automotive instrument panels.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 - 1.20 g/cc | 1.16 - 1.20 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm
|
0.0030 - 0.0040 in/in
|
ASTM D955 |
| Melt Flow | 4.0 g/10 min
|
4.0 g/10 min
|
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 88.3 MPa
|
12800 psi
|
5mm/min; ASTM D638 |
| Elongation at Break | 6.0 %
|
6.0 %
|
5mm/min; ASTM D638 |
| Flexural Yield Strength | 137 MPa
|
19900 psi
|
1.3mm/min; ASTM D790 |
| Flexural Modulus | 4.81 GPa
|
697 ksi
|
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | >= 0.981 J/cm
|
>= 1.84 ft-lb/in
|
ASTM D256 |
PC/ABS LUPOY GP5100
PC/ABS，聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，是由聚碳酸酯（Polycarbonate）和聚丙烯腈（ABS）合金而成的热可塑性塑胶，结合了两种材料的优异特性，ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线（UV）等性质，可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上。
性能
1、一般性能
ABS工程塑料外观为不透明呈象牙色粒料，其制品可着成五颜六色，并具有高光泽度。ABS相对密度为1.05左右，吸水率低。ABS同其他材料的结合性好，易于表面印刷、涂层和镀层处理。ABS的氧指数为18~20，属易燃聚合物，火焰呈黄色，有黑烟，并发出特殊的肉桂味。
2、力学性能
ABS有优良的力学性能，其冲击强度极好，可以在极低的温度下使用：ABS的耐磨性优良，尺寸稳定性好，又具有耐油性，可用于中等载荷和转速下的轴承。ABS的耐蠕变性比PSF及PC大，但比PA及POM小。ABS的弯曲强度和压缩强度属塑料中较差的。ABS的力学性能受温度的影响较大。
3、热学性能
ABS的热变形温度为93~118℃，制品经退火处理后还可提高10℃左右。ABS在-40℃时仍能表现出一点的韧性，可在-40~100℃的温度范围内使用。
4、电学性能
ABS的电绝缘性较好，并且几乎不受温度、湿度和频率的影响，可在大多数环境下使用。
5、环境性能
ABS不受水、无机盐、碱及多种酸的影响，但可溶于酮类、醛类及氯代烃中，受冰乙酸、植物油等侵蚀会产生应力开裂。ABS的耐候性差，在紫外光的作用下易产生降解；于户外半年后，冲击强度下降一半