Technical Datasheet | Supplied by LG Chem

Lupoy? GP1000SW is a general purpose polycarbonate grade by LG Chem. Exhibits high performance, transparency and high flow. Lupoy? GP1000SW is suitable for processing by injection molding. Used in automotive interiors and keypads for mobile phones. Complies with UL 94 HB flame rating.

Physical Properties	Metric	English	Comments
Specific Gravity	1.20 g/cc	1.20 g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow	0.0050 - 0.0080 cm/cm @Thickness 3.20 mm	0.0050 - 0.0080 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	13 g/10 min @Load 1.20 kg, Temperature 300 °C	13 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength, Yield	60.8 MPa @Thickness 3.20 mm	8820 psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	>= 150 % @Thickness 3.20 mm	>= 150 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	103 MPa @Thickness 3.20 mm	14900 psi @Thickness 0.126 in	10mm/min; ASTM D790
Flexural Modulus	2.26 GPa @Thickness 3.20 mm	327 ksi @Thickness 0.126 in	10mm/min; ASTM D790
Izod Impact, Notched	>= 7.45 J/cm @Thickness 3.20 mm, Temperature 23.0 °C	>= 14.0 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F	ASTM D256

PC LUPOY GP1000SW

特性:

为非结晶性热塑性塑料，优质的耐热性能、良好的透明度和极高的耐冲击强度等物理机械性能。

优点：

1．具高强度及弹性系数、高冲击强度、使用温度范围广；

2．高度透明性及自由染色性；

3．H.D.T.高；

4．耐疲劳性差；

5、耐候性佳；

6．电气特性优；

7．无味无臭对人体无害符合卫生安全；

8．成形收缩率低、尺寸安定性良好。

应用

PC工程塑料的三大应用领域是玻璃装配业、汽车工业和电子、电器工业，其次还有工业机械零件、光盘、包装、计算机等办公室设备、医疗及保健、薄膜、休闲和防护器材等。PC可用作门窗玻璃，PC层压板广泛用于银行、使馆、拘留所和公共场所的防护窗，用于飞机舱罩，照明设备、工业安全档板和防弹玻璃。

汽车制造业

聚碳酸酯具有良好的抗冲击、抗热畸变性能，而且耐候性好、硬度高，因此适用于生产轿车和轻型卡车的各种零部件，其主要集中在照明系统、仪表板、加热板、除霜器及聚碳酸酯合金制的保险杠等。

建材行业

聚碳酸酯板材具有良好的透光性，抗冲击性，耐紫外线辐射及其制品的尺寸稳定性和良好的成型加工性能，使其比建筑业传统使用的无机玻璃具有明显的技术性能优势。中国建有聚碳酸酯建材中空板生产线20余条，年需用聚碳酸酯7万吨左右，到2005年达到14万吨。

PC LUPOY GP1000SW 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！