PC LUPOY GP2300

Material Notes:

Description: Injection Molding, PC+GF30%, General Purpose, Heat ResistanceApplication: IT/OA, E&E Housing and Components, Automotive (Interior)CAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical

Physical Properties	Metric	English	Comments
Specific Gravity	1.43 g/cc	1.43 g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Thickness 3.20 mm	0.0010 - 0.0030 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	14 g/10 min @Load 1.20 kg, Temperature 300 ?°C	14 g/10 min @Load 2.65 lb, Temperature 572 ?°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength, Yield	118 MPa @Thickness 3.20 mm	17100 psi @Thickness 0.126 in	5mm/min; ASTM D638
Elongation at Break	4.0 % @Thickness 3.20 mm	4.0 % @Thickness 0.126 in	5mm/min; ASTM D638
Flexural Yield Strength	177 MPa @Thickness 3.20 mm	25600 psi @Thickness 0.126 in	10mm/min; ASTM D790
Flexural Modulus	7.35 GPa @Thickness 3.20 mm	1070 ksi @Thickness 0.126 in	10mm/min; ASTM D790
Izod Impact, Notched	>= 1.08 J/cm @Thickness 3.20 mm, Temperature 23.0 ?°C	>= 2.02 ft-lb/in @Thickness 0.126 in, Temperature 73.4 ?°F	ASTM D256

PC LUPOY GP2300

特性:

为非结晶性热塑性塑料，优质的耐热性能、良好的透明度和极高的耐冲击强度等物理机械性能。

优点：

1．具高强度及弹性系数、高冲击强度、使用温度范围广；

2．高度透明性及自由染色性；

3．H.D.T.高；

4．耐疲劳性差；

5、耐候性佳；

6．电气特性优；

7．无味无臭对人体无害符合卫生安全；

8．成形收缩率低、尺寸安定性良好。

应用

PC工程塑料的三大应用领域是玻璃装配业、汽车工业和电子、电器工业，其次还有工业机械零件、光盘、包装、计算机等办公室设备、医疗及保健、薄膜、休闲和防护器材等。PC可用作门窗玻璃，PC层压板广泛用于银行、使馆、拘留所和公共场所的防护窗，用于飞机舱罩，照明设备、工业安全档板和防弹玻璃。

汽车制造业

聚碳酸酯具有良好的抗冲击、抗热畸变性能，而且耐候性好、硬度高，因此适用于生产轿车和轻型卡车的各种零部件，其主要集中在照明系统、仪表板、加热板、除霜器及聚碳酸酯合金制的保险杠等。

建材行业

聚碳酸酯板材具有良好的透光性，抗冲击性，耐紫外线辐射及其制品的尺寸稳定性和良好的成型加工性能，使其比建筑业传统使用的无机玻璃具有明显的技术性能优势。中国建有聚碳酸酯建材中空板生产线20余条，年需用聚碳酸酯7万吨左右，到2005年达到14万吨。

PC LUPOY GP2300 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！