Borealis PP HJ325MO 低翘曲性 高刚性 PP

¥ 7.68

  • ≥ 25 起订量
  • 10000公斤 总供应
  • 广东 东莞 所在地
东莞市常平平治塑胶原料贸易行
产品详情

HJ325MO is a polypropylene homopolymer intended for injection moulding. Its very high melt flow makes it especially suitable for thin-wall packaging and products with long flow length. is designed for high-speed injection moulding and contains nucleating and antistatic additives. The additives are optimized to provide reduced tendency for mould plate-out. 

This polymer is a CR (controlled rheology) grade with narrow molecular weight distribution giving low warpage. Components moulded from this grade show good ejectability and combine good stiffness with good transparency and gloss, good antistatic properties and good impact strength at ambient temperatures. 

Applications

  • Thin wall containers

  • Square containers

  • Rectangular and flat products, like lids and trays

  • Caps and closures


Special features

  • Good stiffness

  • Good impact strength

  • Excellent antistatic properties

  • Improved gloss and excellent transparency

总览

材料状态 

  • 已商用:当前有效

资料 1 

搜索 UL 黄卡 

供货地区 

北美洲非洲和中东拉丁美洲欧洲亚太地区

添加剂 

成核剂抗静电性 

特性 

成核的低翘曲性高刚性高光均聚物抗静电性可控流变快的成型周期良好抗撞击性流动性高清晰度,高脱模性能良好窄分子量分布

用途 

薄壁容器盖子护罩容器外壳支架托盘

形式 

  • 粒子

加工方法 

  • 注射成型

物理性能

额定值

单位制

测试方法

密度

0.905

g/cm3

ISO 1183

熔流率(熔体流动速率) (230°C/2.16 kg)

50

g/10 min

ISO 1133

收缩率

1.0 到 2.0

%

内部方法
机械性能

额定值

单位制

测试方法

拉伸模量

1650

MPa

ISO 527-2/1

拉伸应力 (屈服)

35.0

MPa

ISO 527-2/50

拉伸应变 (屈服)

9.0

%

ISO 527-2/50

弯曲模量

1350

MPa

ISO 178
冲击性能

额定值

单位制

测试方法

简支梁缺口冲击强度 (23°C)

2.0

kJ/m2

ISO 179/1eA
热性能

额定值

单位制

测试方法

热变形温度 2 (0.45 MPa, 未退火)

100

°C

ISO 75-2/B
注射

额定值

单位制


加工(熔体)温度

210 到 250

°C


模具温度

10 到 30

°C


注射速度

快速



保压

20.0 到 50.0

MPa


备注