Styrolution PS 542N

Technical Datasheet | Supplied by INEOS Styrolution (INEOS Group)

Styrolution? PS 542N by INEOS Styrolution Group is a low odor, impact modified, heat stabilized, high impact polystyrene (PS) grade. It can be processed using sheet extrusion and thermoforming. Styrolution? PS 542N is recommended for packaging.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in?3	ISO 1183
Moisture Absorption at Equilibrium	<= 0.10 % @Temperature 23.0 ?°C	<= 0.10 % @Temperature 73.4 ?°F	50% RH; ISO 62
Water Absorption at Saturation	<= 0.10 % @Temperature 23.0 ?°C	<= 0.10 % @Temperature 73.4 ?°F	ISO 62
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ISO 294-4
Melt Flow	4.1 g/10 min @Load 5.00 kg, Temperature 200 ?°C	4.1 g/10 min @Load 11.0 lb, Temperature 392 ?°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	120 MPa	17400 psi	ISO 2039-1
Tensile Strength, Yield	25.0 MPa	3630 psi	ISO 527
Elongation at Break	45 %	45 %	ISO 527
Elongation at Yield	1.8 %	1.8 %	ISO 527
Tensile Modulus	1.75 GPa	254 ksi	ISO 527
Flexural Strength	40.0 MPa	5800 psi	ISO 178
Charpy Impact Unnotched	0.800 J/cm?2	3.81 ft-lb/in?2	ISO 179

HIPS STYROLUTION 542N

性能

HIPS具有通用聚苯乙烯（GPPS）的尺寸稳定性，而且具有更好的冲击强度和刚性。  

HIPS相对密度为1.04~1.06，热变形温度70~84℃。HIPS的拉伸强度约为15~30MPa，伸长率为35~60%。随温度的降低、应变速率的增加而增加，有点像橡胶增韧体系。HIPS的性质有点像黏弹性固体，当暴露在恒定拉伸应力下会产生蠕变。蠕变随分子量的升高而降低，并通常随橡胶含量的升高而增加。HIPS的蠕变行为强烈依赖于平均分子量(Mw)。弯曲强度为29.4~50 MPa，冲击强度0.09~0.16N/M，维卡软化点84~100℃，熔体指数为2~9g/10min。HIPS部件的耐热性依赖于它们的形状、生产条件、热源类型和加热持续时间，也受HIPS级别的影响。

当暴露在水、碱和稀的无机酸中时，HIPS的性质不受影响。它可被有些有机溶剂溶胀，被另外一些溶解，这是由连续相和溶剂相之间的溶解参数的差异决定的。当暴露在氯代烃和芳香烃中时，HIPS特别容易被破坏。

用途

由于制造方便、成本低，HIPS在许多用具和工业上广泛使用。主要的工业和市场包括包装、一次性用品、用具和消费电器、玩具和娱乐用品、建筑产品和装饰品。HIPS最大的单项应用是包装，尤其是在食品行业中的包装，全世界的消费超过30%。

HIPS STYROLUTION 542N 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！