品 牌:日本宝理
产品型号:TR-20
产 地:日本
性 能:15滑石填料增强;高刚性;低翘曲
特 征:注塑级
Common features of Delrin? acetal resins include mechanical and physical properties such as high mechanical strength and rigidity, excellent fatigue and impact resistance, as well as resistance to moisture, gasoline, lubricants, solvents, and many other neutral chemicals. Delrin? acetal resins also have excellent dimensional stability and good electrical insulating characteristics. They are naturally resilient, self-lubricating, and available in a variety of colors and speciality grades.
物性表
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.53 | g/cm3 | ISO 1183 |
熔流率(熔体流动速率)(190°C/2.16 kg) | 21 | g/10 min | ISO 1133 |
溶化体积流率(MVR)(190°C/2.16 kg) | 16 | cm3/10min | ISO 1133 |
吸水率(23°C, 24 hr) | 0.5 | ISO 62 | |
硬度 | 额定值 | 单位制 | 测试方法 |
洛氏硬度(M 计秤) | 75 | ISO 2039-2 | |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | 4500 | MPa | ISO 527-2 |
拉伸应力 | 59 | MPa | ISO 527-2 |
拉伸应变(断裂) | 5 | ISO 527-2 | |
弯曲模量 | 4100 | MPa | ISO 178 |
弯曲应力 | 96 | MPa | ISO 178 |
摩擦系数 | JIS K7218 | ||
Dynamic3 | 0.34 | ||
与钢 - 动态4 | 0.56 | ||
磨损因数 | JIS K7218 | ||
0.49 MPa, 0.30 m/sec5 | 150 | 10^-8 mm3/N·m | |
0.060 MPa, 0.15 m/sec6 | 500 | 10^-8 mm3/N·m | |
0.060 MPa, 0.15 m/sec7 | 7000 | 10^-8 mm3/N·m | |
0.49 MPa, 0.30 m/sec8 | 8000 | 10^-8 mm3/N·m | |
冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度 | 3 | kJ/m2 | ISO 179/1eA |
热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度(1.8 MPa, 未退火) | 125 | °C | ISO 75-2/A |
线形热膨胀系数 | 内部方法 | ||
流动 : 23 到 55°C | 8.00E-05 | cm/cm/°C | |
横向 : 23 到 55°C | 8.00E-05 | cm/cm/°C | |
电气性能 | 额定值 | 单位制 | 测试方法 |
表面电阻率 | 9.00E 15 | ohms | IEC 60093 |
体积电阻率 | 2.00E 14 | ohms·cm | IEC 60093 |
介电强度(3.00 mm) | 21 | kV/mm | IEC 60243-1 |
可燃性 | 额定值 | 单位制 | 测试方法 |
UL 阻燃等级 | HB | UL 94 | |
补充信息 | 额定值 | ||
Color Number | CF2001 | ||
注射 | 额定值 | 单位制 | |
干燥温度 | 80.0 到 90.0 | °C | |
干燥时间 | 3.0 到 4.0 | hr | |
加工(熔体)温度 | 190 到 210 | °C | |
模具温度 | 60.0 到 80.0 | °C | |
注塑压力 | 49.0 到 98.0 | MPa | |
螺杆转速 | 100 到 150 | rpm |