HIPS STYROLUTION 641F

Styrolution PS 641F is high impact polystyrene with high heat resistance.

• High impact

• High heat resistance

Information provided by Styrolution

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in3	ISO 1183
Moisture Absorption at Equilibrium	<= 0.10 % @Temperature 23.0 °C	<= 0.10 % @Temperature 73.4 °F	50% RH; ISO 62
Water Absorption at Saturation	<= 0.10 % @Temperature 23.0 °C	<= 0.10 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ISO 294-4
Melt Flow	2.5 g/10 min @Load 5.00 kg, Temperature 200 °C	2.5 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	90.0 MPa	13100 psi	ISO 2039-1
Tensile Strength, Yield	28.0 MPa	4060 psi	ISO 527
Elongation at Break	40 %	40 %	ISO 527
Elongation at Yield	1.7 %	1.7 %	ISO 527
Tensile Modulus	2.00 GPa	290 ksi	ISO 527
Flexural Strength	44.0 MPa	6380 psi	ISO 178
Charpy Impact Unnotched	1.40 J/cm2	6.66 ft-lb/in2	ISO 179

HIPS STYROLUTION 641F

聚苯乙烯分子及其聚集态结构决定其为刚硬的脆性材料，在应力作用下表现为脆性断裂。

热性能

聚苯乙烯的特性温度为：脆化温度-30℃左右、玻璃化温度80～105℃、熔融温度为140～180℃、分解温度300℃以上。由于聚苯乙烯的力学性能随温度的升高明显下降、耐热性较差，因而连续使用温度为60℃左右，最高不宜超过80℃。导热率低，为0.04～0.15W/（m·K），几乎不受温度而变化，因而具有良好的隔热性。

电性能

聚苯乙烯具有良好的电性能，体积电阻率和表面电阻率分别高达10^16～10^18Ω·cm和10^15～10^18Ω。介电损耗角正切值极低，并且不受频率和环境温度、湿度变化的影响，是优异电绝缘材料。

光学性能

聚苯乙烯具有优良的光学性能，透光率达88%～92%、折射率为1.59～1.60，可以透过所有波长的可见光，透明性材料在塑料中仅次于有机玻璃等丙烯酸类聚合物。但因聚苯乙稀耐候性较差，长期使用或存放时受阳光、灰尘作用，会出现浑浊、发黄等现象，因而用聚苯乙烯制作光学部件等高透明制品时需考虑加入适当品种和用量的防老剂。

化学性能

耐腐蚀较好，耐溶剂性、耐氧化较差。

用途

聚苯乙烯易加工成型，并具有透明、廉价、刚性、绝缘、印刷性好等优点。可广泛用于轻工市场，日用装璜，照明指示和包装等方面。在电气方面更是良好的绝缘材料和隔热保温材料，可以制作各种仪表外壳、灯罩、光学化学仪器零件、透明薄膜、电容器介质层等。

可用于粉类和乳液类化妆品。用于粉饼有很好的压缩性,可改善粉的黏附性能。赋予皮肤光泽和润滑感,是代替滑石粉和二氧化硅的高级填充剂。

HIPS STYROLUTION 641F 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！