HIPS STYROLUTION 7120
Excellent ESCR to foodstuffs and PUR foams
Good low temperature impact strength
High relative stiffness/potential to down gauge sheet
UL Classification 94 HB
Information provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 2.3 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.3 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 42 | 42 | ASTM D 785 |
| Tensile Strength, Yield | 20.3 MPa | 2950 psi | ASTM D 638 |
| Elongation at Break | 55 % | 55 % | ASTM D 638 |
| Tensile Modulus | 1.79 GPa | 260 ksi | ASTM D 638 |
| Flexural Strength | 44.1 MPa | 6400 psi | ASTM D 790 |
| Flexural Modulus | 1.76 GPa | 255 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D 638 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.5 @Thickness 1.00 mm, Frequency 1.00e+6 Hz |
2.5 @Thickness 0.0394 in, Frequency 1.00e+6 Hz |
ASTM D 150 |
HIPS STYROLUTION 7120
共聚物
它们的韧度非常好。主要品种有：苯乙烯一丙烯腈共聚物（SAN）、苯乙烯一马来酸酐共聚物（SMA）、苯乙烯一丁二烯一苯乙烯共聚物（SBS）、苯乙烯和丙烯酸酯共聚物，以及以它们为基材的改性体。SAN的热变形温度比透明PS高，其耐溶剂性也有改进，具有优异的抗渗透性。橡胶改性的SAN有丙烯睛一丁二烯一苯乙烯共聚物（ABS）和丙烯睛．苯乙烯一丙烯酸酯共聚物（ASA）等树脂。S－MA的热变形温度比透明体PS更高，可达40°F，它有优良的透明性和光泽度。SMA可用橡胶改性或采用玻璃纤维增强。SBS和SBS的各种改性体可作为改善抗冲击性、柔性和流动性的组分用于生产具有粘性和抗弯曲的产品如胶泥、鞋底、沥青毡等，SBS还用于生产透明抗冲击PS。苯乙烯可与丙烯酸酯弹性体共聚生成具有优良物理性能的透明级抗冲击PS。
合成材料
塑料：
聚乙烯；聚氯乙烯；聚苯乙烯；聚乙烯醇；聚丙烯；聚丙烯酸；聚丁烯；聚异丁烯；聚砜；聚甲醛；聚酰胺；聚碳酸酯；聚乳酸；聚四氟乙烯；聚对苯二甲酸乙二酯；环氧树脂；酚醛树脂；聚氨酯
合成橡胶：
合成纤维：
丙纶；涤纶；锦纶；腈纶；氨纶；维尼纶；耐纶；达克纶；克夫纶
抗冲击型
抗冲击聚苯乙烯 它是苯乙烯单体与橡胶接枝聚合生成的无定形聚合物，或是聚苯乙烯与橡胶（通常为聚丁二烯橡胶）的物理共混物。所生成的聚合物具有韧性，通常为白色（也有透明的品级），挤出和成型非常容易。
抗冲击聚苯乙烯性能检测根据其相对的抗冲击强度分为几级：
中等抗冲击品级的缺口悬臂梁抗冲击强度一般为 0.6—1./i；
高抗冲击品级的抗冲击度为1.5—2.5ftlb/in；
极高抗冲击级的抗冲击强度为>2./in