东莞市铭汇塑胶有限公司
产品物性表
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸湿率 | ASTM D-570 | 0.2 | % | |
| 熔融指数 | ASTM D-1238 | 21 | g/10min | ||
| 物理性能 | 比重 | ASTM D-792 | 1.42 | ||
| 磨耗率 | ASTM D-1044 | 13 | mg/1000cycles | ||
| 成型收缩率 | 旭化成方法 | 1.7-2.1 | % | ||
| 机械性能 | 洛氏硬度 | ASTM D-785 | 120 | R Scale | |
| 延伸率 | ASTM D-638 | 45 | % | ||
| 抗挠系数 | ASTM D-790 | 2940 | MPa | ||
| 拉伸强度 | ASTM D-638 | 69 | MPa | ||
| 悬臂梁式缺口冲击强度 | ASTM D-256 | 59 | J/m | ||
| 抗挠强度 | ASTM D-790 | 103 | MPa | ||
| 洛氏硬度 | ASTM D-785 | 94 | M Scale | ||
| 热性能 | 热变形温度 | 0.45MPa | ASTM D-648 | 172 | ℃ |
| 1.82MPa | ASTM D-648 | 136 | ℃ | ||
| 燃烧性 | UL 94 | HB | |||
| 线性膨胀系数 | TMA | 10 | ×10-5cm/cm℃ |
||