Torelina A504X95
Polyphenylene Sulfide
Product Description:
Torelina? A504X95 is a Polyphenylene Sulfide (PPS) product filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America. Typical application: Electrical/Electronic Applications. Primary characteristic: flame rated.
| General | |
Material Status |
|
Literature 1 |
|
UL Yellow Card 2 |
|
Search for UL Yellow Card |
|
Availability |
Asia PacificEuropeNorth America |
Filler / Reinforcement |
|
Features |
|
Uses |
|
Appearance |
BlackNatural Color |
Part Marking Code |
|
| Physical | Nominal Value |
Unit |
Test Method |
Density (23°C) |
1.66 |
g/cm3 |
ISO 1183 |
Molding Shrinkage 3 |
Internal Method | ||
Across Flow : 3.00 mm |
0.80 |
% |
|
Flow : 3.00 mm |
0.20 |
% |
|
Water Absorption (24 hr, 23°C) |
0.020 |
% |
ISO 62 |
| Hardness | Nominal Value |
Unit |
Test Method |
Rockwell Hardness (R-Scale) |
122 |
ISO 2039-2 |
| Mechanical | Nominal Value |
Unit |
Test Method |
Tensile Stress (23°C) |
200 |
MPa |
ISO 527-2 |
Tensile Strain (Break, 23°C) |
1.6 |
% |
ISO 527-2 |
Flexural Modulus (23°C) |
15500 |
MPa |
ISO 178 |
Flexural Stress (23°C) |
290 |
MPa |
ISO 178 |
Shear Strength (23°C) |
75.0 |
MPa |
JIS K7214 |
Coefficient of Friction 4 |
0.25 |
||
Taber Abrasion Resistance (1000 Cycles) |
50.0 |
mg |
ISO 9352 |
| Impact | Nominal Value |
Unit |
Test Method |
Charpy Notched Impact Strength (23°C) |
11 |
kJ/m2 |
ISO 179 |
Charpy Unnotched Impact Strength (23°C) |
45 |
kJ/m2 |
ISO 179 |
| Thermal | Nominal Value |
Unit |
Test Method |
Heat Deflection Temperature (1.8 MPa, Unannealed) |
260 |
°C |
ISO 75-2/A |
Melting Temperature |
278 |
°C |
ISO 11357-3 |
CLTE |
ISO 11359-2 | ||
Flow |
2.3E-5 |
cm/cm/°C |
|
Transverse |
3.1E-5 |
cm/cm/°C |
| Electrical | Nominal Value |
Unit |
Test Method |
Volume Resistivity |
1.0E+14 |
ohms·cm |
IEC 60093 |
Electric Strength |
25 |
kV/mm |
IEC 60243-1 |
Dielectric Constant 5 (23°C, 1 MHz) |
3.60 |
IEC 60250 | |
Dissipation Factor 5 (23°C, 1 MHz) |
2.0E-3 |
IEC 60250 | |
| Flammability | Nominal Value |
Unit |
Test Method |
Flame Rating (0.28 mm) |
V-0 |
UL 94 |
| Additional Information | Nominal Value |
Unit |
Test Method |
Bar Flow Length 6 (320°C, 1.00 mm) |
150 |
mm |
Internal Method |
日本东丽PPS A504 添加40%玻璃纤维
日本东丽PPS A504X90 高抗冲击，高韧性 高强度 添加40%玻璃纤维
日本东丽PPS A504X95 高流动，低闪点 添加40%玻璃纤维
日本东丽PPS A503 高流动 添加30%玻璃纤维
日本东丽PPS A604 高韧性 添加40%玻璃纤维
日本东丽PPS A310M 高强度，低翘曲 添加70%玻璃纤维 矿物填充
日本东丽PPS A310MX04 标准级 添加65%玻璃纤维 矿物填充
日本东丽PPS A610M 高流动 添加60%玻璃纤维 矿物填充
日本东丽PPS A610MX03 高韧性 添加65%玻璃纤维 矿物填充
日本东丽PPS A515 超耐磨 添加30%PTFE
日本东丽PPS A756MX02 抗静电 添加65%玻璃纤维 矿物填充
日本宝理PPS 0220A9 超高韧性 纯PPS V0
日本宝理PPS 1130A64 标准 低溢料 添加30%玻璃纤维 V0
日本宝理PPS 1140A64 标准 低溢料 添加40%玻璃纤维 V0
日本宝理PPS 1150A64 低翘曲 低溢料 添加50%玻璃纤维 玻璃鳞片 V0
日本宝理PPS 1140A7 超高流动性 添加40%玻璃纤维 V0
日本宝理PPS 1140A6 高强度 添加40%玻璃纤维 V0
日本宝理PPS 1130A1 超高韧性 添加30%玻璃纤维 V0
日本宝理PPS 1140A1 超高韧性 添加40%玻璃纤维 V0
日本宝理PPS 1140A66 低氯 添加40%玻璃纤维 V0
日本宝理PPS 6165A6 尺寸精度优良 添加65%矿物/玻璃纤维 V0
日本宝理PPS 6165A7 尺寸精度优良 添加60%矿物/玻璃纤维 V0
日本宝理PPS 6465A6 低翘曲 高光泽 添加65%矿物/玻璃纤维 V0
日本宝理PPS 6465A62 低翘曲 高光泽 添加60%矿物/玻璃纤维 V0
日本宝理PPS 6565A6 低温模具 良好树脂间粘接性 添加65%矿物/玻璃纤维 V0
日本宝理PPS 6565A7 低温模具 良好树脂间粘接性 添加60%矿物/玻璃纤维 V0
日本宝理PPS 0220U9 高耐冲击
日本宝理PPS 1130T6 高耐冲击 添加30%碳纤维 V2
日本宝理PPS 6150T6 高耐冲击 添加50%矿物/玻璃纤维填充
日本宝理PPS 3130A1 滑动性 耐磨损 添加30%矿物填料 V0
日本宝理PPS 6345A4 滑动性 耐磨损 添加30%玻璃纤维 V0 PTFE润滑剂
日本宝理PPS 7140A4 导电 耐磨损 添加30%碳纤维 V0 PTFE润滑剂
日本宝理PPS 2130A1 导电 耐磨损 添加30%碳纤维 V0
日本宝理PPS 7340A4 导电 添加45%矿物/碳/玻璃纤维填充 V1
1140A6 加纤40% 低闪点1140A64