苏州柯远化工科技有限公司
SABIC沙伯基础塑料LEXAN 505RU聚碳酸酯（PC）是一种可注塑的非氯化和非溴化阻燃级产品，填充10％玻璃纤维, 紫外线稳定，阻燃等级为UL94 V0@1.5mm。
我司经销Sabic Lexan PC Sabic Valox PBT Sabic Cycoloy PC/ABS Sabic Xenoy PC/PBT Sabic Noryl PPO
材料。所有品牌材料承诺原厂原包。
SABIC 505RU的物性数据如下：
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 74 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 62 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 4 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 6 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 3600 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 114 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3200 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 72 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 60 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 6 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 3500 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 122 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3500 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, unnotched, 23°C | 1200 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 90 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 70 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 25 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | NB75 | kJ/m2 | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | 73 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 10 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 8 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 7 | kJ/m2 | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB87 | kJ/m2 | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB85 | kJ/m2 | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 149 | °C | ASTM D 1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 137 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 5.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 7.4E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 5.E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | Pass | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 147 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 149 | °C | ISO 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 136 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.26 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.4-0.6 | % | SABIC method | |
| Melt Flow Rate, 300°C/1.2 kgf | 8 | g/10 min | ASTM D 1238 | |
| Density | 1.26 | g/cm3 | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.3 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 7 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | ||||
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
| Comparative Tracking Index | 175 | V | IEC 60112 | |
| FLAME CHARACTERISTICS | ||||
| UL Compliant, 94V-2 Flame Class Rating | 0.75 | mm | UL 94 by SABIC-IP | |
| UL Compliant, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 by SABIC-IP | |
| UL Compliant, 94-5VA Rating | 3 | mm | UL 94 by SABIC-IP | |
| UL Compliant, 94-5VB Rating | 3 | mm | UL 94 by SABIC-IP | |
| Glow Wire Flammability Index 960°C, passes at | 0.75 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 850 | °C | IEC 60695-2-13 | |
| Glow Wire Ignitability Temperature, 3.0 mm | 875 | °C | IEC 60695-2-13 | |
| UV-light, water exposure/immersion | F1 | - | UL 746C | |
| Injection Molding | ||||
| Drying Temperature | 120 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 290-320 | °C | ||
| Nozzle Temperature | 280-310 | °C | ||
| Front - Zone 3 Temperature | 290-320 | °C | ||
| Middle - Zone 2 Temperature | 280-310 | °C | ||
| Rear - Zone 1 Temperature | 270-300 | °C | ||
| Hopper Temperature | 60-80 | °C | ||
| Mold Temperature | 80-120 | °C |