PMMA PLEXIGLAS 7N

Description: PLEXIGLAS? 7N is a molding compound based on polymethyl methacrylate (PMMA). Typical properties of PLEXIGLAS? molding compounds are:

• good flow

• high mechanical strength, surface hardness and abrasion resistance

• high light transmission

• excellent weather resistance

• free colorability due to crystal clarity

The special properties of PLEXIGLAS? 7N compound are:

• very good mechanical properties

• high heat deflection temperature

• very good flow / melt viscosity

• AMECA listing

Application: Used for injection molding optical and technical items.

The former Evonik Methacrylates business has been sold to R?hm GmbH.

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in3	ISO 1183
Melt Flow	7.14 g/10 min @Load 3.80 kg, Temperature 230 °C	7.14 g/10 min @Load 8.38 lb, Temperature 446 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	73.0 MPa	10600 psi	5 mm/min; ISO 527
Elongation at Break	3.5 %	3.5 %	5 mm/min; ISO 527
Tensile Modulus	3.20 GPa	464 ksi	1 mm/min; ISO 527
Charpy Impact Unnotched	2.00 J/cm2 @Temperature 23.0 °C	9.52 ft-lb/in2 @Temperature 73.4 °F	ISO 179
Thermal Properties	Metric	English	Comments
CTE, linear	80.0 μm/m-°C @Temperature 0.000 - 50.0 °C	44.4 μin/in-°F @Temperature 32.0 - 122 °F	ASTM E831
Deflection Temperature at 0.46 MPa (66 psi)	100 °C	212 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	95.0 °C	203 °F	ISO 75
Vicat Softening Point	103 °C	217 °F	B50; ISO 306
Glass Transition Temp, Tg	110 °C	230 °F	IEC 10006
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	IEC 707
Optical Properties	Metric	English	Comments
Refractive Index	1.49	1.49	ISO 489
Haze	<= 0.50 %	<= 0.50 %	ASTM D1003
Transmission, Visible	92 %	92 %	Transmission Factor; DIN 5036

PMMA PLEXIGLAS 7N 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！

PMMA原料的特性：

无色透明，透光率达90%---92%，韧性强，比硅玻璃大10倍以上。

光学性、绝缘性、加工性及耐候性佳。

溶解于四氯化碳、苯、甲苯二氯乙烷、三氯甲烷和丙酮等有机溶剂。

具有较高透明度和光亮度，耐热性好，并有坚韧，质硬，刚性特点，热变形温度80℃，弯曲强度110Mpa。

密度1.14—1.20g/cc,变形温度76--116℃，成型收缩率0.2—0.8%。

线膨胀系数0.00005—0.00009/℃,热变形温度68--69℃(74--107℃)

PMMA用途

PMMA具有质轻、价廉，易於成型等优点。溶于有机溶剂如苯甲醚等，可以形成良好的薄膜和良好的介电性能，可以作为有机场效应管的介质层。 [1] 

它的成型方法有浇铸，射出成型，机械加工、热成型等。尤其是射出成型，可以大批量生产，制程简单，成本低。因此，它的应用日趋广泛，它广泛用于仪器仪表零件、汽车车灯、光学镜片、透明管道。

有机玻璃压克力（亚克力）在建筑业中的应用在建筑方面，有机玻璃压克力（亚克力）主要应用于建筑采光体、透明屋顶、棚顶、电话亭、楼梯和房间墙壁护板等方面；卫生洁具方面有浴缸、洗脸盆、化妆台等产品。在高速公路及高等级道路照明灯罩及汽车灯具方面的应用发展也相当快。其中，建筑采光体、浴缸、街头广告灯箱和电话亭等方面的市场增长较快，今后的发展空间较大，市场前景十分广阔。