上海江尚塑胶材料有限公司
EMA热塑弹性体现货 采购认准江尚塑胶, 上海江尚塑胶专业从事国内外塑胶原料进出口销售及批发业务,塑胶原料专业供应商,品类齐全,现货供应,闪电发货,价格实惠, 货源稳定,售后完善,欢迎来电订购!
【上海江尚公司主营】：通用塑料,工程塑料,热塑弹体,热固性塑料等
热塑弹性体EMA:
| Lotryl?range | |||||||||||
| The data displayed in the tables below are typical values but should not be considered as commercial specifications. | |||||||||||
| Grades | Acrylate content | Melt | Melting point | Vicat | Ring and ball | Tensile strength | Elonga- | Flex. | Hard- | Hard- | Density |
| (%) | index | (C°) | T° | T° | at break | tion | Modul. | ness | ness | (g/cm3) | |
| (g/10min) | (C°) | (C°) | (MPa) | at break | (MPa) | Shore | Shore | ||||
| (%) | A | D | |||||||||
| BestPeel 2012 | 20 | 11 | 79 | 42 | - | 9 | 700 | 25 | 84 | 21 | 0.95 |
| BestPeel 2407 | 22-25 | 1月3日 | 72 | 40 | - | - | 800 | - | 79 | - | 0.94 |
| 17BA04 | 16-19 | 3.5-4.5 | 93 | 60 | - | 15 | 700 | 45 | - | 32 | 0.93 |
| 28BA175 | 26-30 | 150-200 | 80 | 40 | 94 | 3 | 300 | 23 | 80 | - | 0.93 |
| 30BA02 | 27-32 | 1.5-2.5 | 78 | 41 | 190 | 6 | 850 | 9 | 75 | - | 0.93 |
| 35BA40 | 33-37 | 35-45 | 66 | 40 | 110 | 2 | 600 | - | 70 | - | 0.93 |
| 35BA320 | 33-37 | 260-350 | 65 | 40 | 85 | 1.5 | 200 | - | 52 | - | 0.93 |
| 18MA02 | 17-20 | 2月3日 | 83 | 53 | - | 13 | 700 | 50 | - | 25 | 0.94 |
| 20MA08 | 19-21 | 7月9日 | 80 | 46 | - | 9 | 800 | 20 | 83 | - | 0.94 |
| 24MA005 | 23-26 | 0.4-0.7 | 72 | 45 | - | 17 | 750 | 18 | 84 | - | 0.94 |
| 24MA02 | 23-26 | 1月3日 | 68 | 40 | - | 9 | 800 | 12 | 79 | 22 | 0.94 |
| 28MA07 | 26-30 | 6月8日 | 65 | 40 | 7 | 900 | 10 | 76 | - | 0.95 | |
| 29MA03 | 27-31 | 2.0-3.5 | 61 | 40 | 175 | 6 | 900 | 10 | 75 | - | 0.95 |
| Lotader?GMA grades | |||||||||||
| Grades | Glycidyl methacrylate content (%Wt) | Methyl acrylate content (%Wt) | Melt Index (g/10min) | Melting point (°C) | Vicat point (°C) | Tensil strengh at break (MPa) | Elongation at break (%) | Hardness shore D | |||
| AX8820 | 4.5 | 0 | 2 | 107 | 88 | - | - | - | |||
| AX8840 | 8 | 0 | 5 | 104 | 87 | 8 | 400 | 50 | |||
| AX8900 | 8 | 24 | 6 | 65 | 40 | 4 | 1100 | 18 | |||
| AX8930 | 3 | 25 | 7 | -65 | 40 | ||||||