PS TAIRIREX GP5250

General

Material Status 

  • Commercial: Active

Availability 

Asia PacificEuropeNorth America

Features 

  • General Purpose

Uses 

  • General Purpose

Agency Ratings 

RoHS Compliance 

UL File Number 

  • E162823

Processing Method 

  • Injection Molding

Physical

Nominal Value

Unit

Test Method

Density / Specific Gravity 2



ASTM D792

Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)


g/10 min

ASTM D1238
Mechanical

Nominal Value

Unit

Test Method

Tensile Modulus (73°F)


psi

ASTM D638

Tensile Strength (73°F)


psi

ASTM D638

Tensile Elongation (Break, 73°F)


%

ASTM D638

Flexural Modulus (73°F)


psi

ASTM D790

Flexural Strength (73°F)


psi

ASTM D790
Impact

Nominal Value

Unit

Test Method

Unnotched Izod Impact 3 (73°F)


ft·lb/in

ASTM D256
Thermal

Nominal Value

Unit

Test Method

Deflection Temperature Under Load 4 (264 psi, Annealed)


°F

ASTM D648

Vicat Softening Temperature 5


°F

ASTM D1525

PS TAIRIREX GP5250

力学性能

聚苯乙烯分子及其聚集态结构决定其为刚硬的脆性材料,在应力作用下表现为脆性断裂。

热性能

聚苯乙烯的特性温度为:脆化温度-30℃左右、玻璃化温度80~105℃、熔融温度为140~180℃、分解温度300℃以上。由于聚苯乙烯的力学性能随温度的升高明显下降、耐热性较差,因而连续使用温度为60℃左右,最高不宜超过80℃。导热率低,为0.04~0.15W/(m·K),几乎不受温度而变化,因而具有良好的隔热性。

电性能

聚苯乙烯具有良好的电性能,体积电阻率和表面电阻率分别高达10^16~10^18Ω·cm和10^15~10^18Ω。介电损耗角正切值极低,并且不受频率和环境温度、湿度变化的影响,是优异电绝缘材料。

光学性能

聚苯乙烯具有优良的光学性能,透光率达88%~92%、折射率为1.59~1.60,可以透过所有波长的可见光,透明性材料在塑料中仅次于有机玻璃等丙烯酸类聚合物。但因聚苯乙稀耐候性较差,长期使用或存放时受阳光、灰尘作用,会出现浑浊、发黄等现象,因而用聚苯乙烯制作光学部件等高透明制品时需考虑加入适当品种和用量的防老剂。

化学性能

耐腐蚀较好,耐溶剂性、耐氧化较差。


用途

聚苯乙烯易加工成型,并具有透明、廉价、刚性、绝缘、印刷性好等优点。可广泛用于轻工市场,日用装璜,照明指示和包装等方面。在电气方面更是良好的绝缘材料和隔热保温材料,可以制作各种仪表外壳、灯罩、光学化学仪器零件、透明薄膜、电容器介质层等。

可用于粉类和乳液类化妆品。用于粉饼有很好的压缩性,可改善粉的黏附性能。赋予皮肤光泽和润滑感,是代替滑石粉和二氧化硅的高级填充剂。

PS TAIRIREX GP5250 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料,价格最优,质量保证!



首页 橡塑 / 通用塑料 / PS
相关产品
店内推荐
首页
店铺
拨打电话 立即报价
发送询价单
采购商品:
采购数量:
联系信息:
公司名称:
采购说明:
 
您的询盘第一时间将不发送给其他供应商,但该供应商24 小时未响应情况下,仍将为您分配更合适供应商
图形验证:
图形验证码 换一换
验证码校验