TAIRILAC ABS ANC100

Technical Datasheet | Supplied by Formosa Chemicals & Fiber

TAIRILAC ABS ANC100 by Formosa Chemicals & Fiber is a flame retardant, self extinguishing acrylonitrile butadiene styrene (ABS) grade. Available in the form of pellets. Can be processed by injection molding. Used in housing of LCD monitor, LCD-TV computers & OA machine. Complies with REACH, SGS, UL rating, SONY standard (SS-00259) and certificates of environmental protection. TAIRILAC ABS ANC100 by Formosa Chemicals & Fiber also meets with the Directives of RoHS 2002/95/EC, 2003/11/EC, EN71 part 3 and 2011/65/EU Annex II.

抗張強度 Tensile Strength	kg/cm2 ( MPa)	ASTM D-638 ( ISO527)	23℃	390 (38)
彎曲強度 Flexural Strength	kg/cm2 ( MPa)	ASTM D-790 ( ISO178)	23℃	620 (61)
彎曲模數 Flexural Modulus	kg/cm2 ( MPa)	ASTM D-790 ( ISO178)	23℃	24000 (2350)
洛式硬度 Rockwell Hardness	R-Scale	ASTM D-785 ( ISO2039/2 )	23℃	R-101
Izod衝擊強度 Izod Impact Strength	kg-cm/cm ( J/m )	ASTM D-256 ( ISO R180 )	23℃ 1/4'' 厚	18 (176)
衛氏軟化點 Vicat Softening Point	℃	ASTM D-1525 (ISO 306)	1 Kg Load	84

ABS TAIRILAC ANC100

（1）力学性能

ABS有优良的力学性能，其冲击强度较好，可以在极低的温度下使用。即使ABS制品被破坏，也只能是拉伸破坏而不会是冲击破坏。ABS的耐磨性能优良，尺寸稳定性好，又具有耐油性，可用于中等载荷和转速下的轴承。ABS的蠕变性比PSF及PC大，但比PA和POM小。ABS的弯曲强度和压缩强度属塑料中较差的。ABS的力学性能受温度的影响较大。

（2）热学性能

ABS属于无定形聚合物，无明显熔点；熔体粘度较高，流动性差，耐候性较差，紫外线可使变色；热变形温度为70—107℃（85左右），制品经退火处理后还可提高10℃左右。对温度，剪切速率都比较敏感；ABS在－40℃时仍能表现出一定的韧性，可在 -40℃到85℃的温度范围内长期使用。

应用：

1、汽车产业

汽车产业中有众多零件是用ABS或ABS合金制造的，如上海的桑塔纳轿车，每辆车用ABS11kg，位列汽车中所用塑料第三。在其它车辆中，ABS的使用量也颇惊人。2000年我国就汽车用ABS的量就达到3.5万吨。轿车中主要零部件使用ABS的如仪表板用PC/ABS作骨架，表面再复以PVC/ABS/BOVC制成的薄膜。此外，车内装饰件大量使用了ABS，如手套箱、杂物箱总成是用耐热ABS制成，门槛上下饰件、水箱面罩用ABS制成，另外还有很多零件采用ABS为原料。

2、办公室机器

由于ABS有高的光泽和易成型性，办公室设备机器需要有漂亮的外观，有良好的手感，如电话机外壳、存储器外壳以及计算机、传真机、复印机中都大量使用了ABS制作的零件。

3、家用电器

由于ABS有高的光泽和易成型性，所以在家电和小家电中更有着广泛的市场，如家用传真机、音响、VCD中也大量选用ABS为原料，吸尘器中也使用了很多ABS制作的零件，厨房用具也大量使用了ABS制作的零件。