| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | — | ASTM D-792 | 1.42 | — | |
| 吸水量 | 24小时浸渍 | ASTM D-570 | 0.25 | % | ||
| 吸水量 | 50%相对湿度 | ASTM D-570 | 0.22 | % | ||
| 吸水量 | 浸渍平衡点 | ASTM D-570 | 0.90 | % | ||
| 自燃性 | — | UL 94 | HB | — | ||
| 机械性能 | 模收缩 | — | — | 2.2-2.4 | % | |
| 洛氏硬度 | — | ASTM D-785 | 94 | M scale | ||
| 洛氏硬度 | — | ASTM D-785 | 120 | R scale | ||
| 介电强度 | 瞬间Short time(2.3mm) | ASTM D-149 | 19.7 | kv/mm | ||
| 线性热膨胀系数 | 104～160℃ | ASTM D-696 | 14.9 | 10m/m℃ | ||
| 拉伸强度 | -55℃ | ASTM D-638 | 101 | MPA | ||
| 拉伸强度 | 23℃ | ASTM D-638 | 69 | MPa | ||
| 拉伸强度 | 70℃ | ASTM D-638 | 48 | MPa | ||
| 拉伸强度 | 100℃ | ASTM D-638 | 36 | MPa | ||
| 拉伸强度 | 122℃ | ASTM D-638 | 26 | MPa | ||
| 破裂点拉伸变形量 | -55℃ | ASTM D-638 | 40 | % | ||
| 破裂点拉伸变形量 | 23℃ | ASTM D-638 | 65 | % | ||
| 破裂点拉伸变形量 | 70℃ | ASTM D-638 | 230 | % | ||
| 破裂点拉伸变形量 | 100℃ | ASTM D-638 | >260 | % | ||
| 破裂点拉伸变形量 | 122℃ | ASTM D-638 | >260 | % | ||
| 弹性系数 | 23℃ | ASTM D-638 | 3220 | MPa | ||
| 挠曲系数 | -55℃ | ASTM D-790 | 4120 | MPa | ||
| 挠曲系数 | 23℃ | ASTM D-790 | 2840 | MPa | ||
| 挠曲系数 | 70℃ | ASTM D-790 | 1580 | MPa | ||
| 挠曲系数 | 100℃ | ASTM D-790 | 1030 | MPa | ||
| 挠曲系数 | 122℃ | ASTM D-790 | 685 | MPa | ||
| 挠曲变形强度 | 23℃ | ASTM D-790 | 98 | MPa | ||
| 压缩应力 | 23℃,1%变形 | ASTM D-695 | 35 | MPa | ||
| 压缩应力 | 23℃,10%变形 | ASTM D-695 | 123 | MPa | ||
| 抗剪强度 | 23℃ | ASTM D-732 | 66 | MPa | ||
| 挠曲疲劳忍耐限度 | 50%RH,23℃,10周期 | ASTM D-671 | 32 | MPa | ||
| 负载变形量 | 140kg/cm,50℃ | ASTM D-621 | 0.5 | % | ||
| 抗拉伸冲击强度 | 长试片23℃ | ASTM D-1822 | 525 | kj/m | ||
| IZOD冲击试验 | 无缺口23℃ | ASTM D-256 | >5300 | j/m | ||
| IZOD冲击试验 | 缺口-40℃ | ASTM D-256 | 98 | j/m | ||
| IZOD冲击试验 | 23℃ | ASTM D-256 | 137 | j/m | ||
| 热畸变温度 | 0.5MPa | ASTM D-648 | 172 | ℃ | ||
| 电气性能 | 介电常数 | 50%RH,23℃,10～10Hz | ASTM D-150 | 3.7 | Ω.cm | |
| 介电因数 | 50%RH,23℃,10Hz | ASTM D-150 | 0.005 | — | ||
| 容积电阻率 | 23℃,0.2%含水量 | ASTM D-257 | 1×10 | Ω.cm | ||
| 抗电弧 | 3.1mm | ASTM D-495 | 220 | sec | ||
| 热 性 能 | 线性热膨胀系数 | 60～104℃ | ASTM D-696 | 13.7 | 10m/m℃ | |
| 热畸变温度 | 1.8MPa | ASTM D-648 | 136 | ℃ | ||
| 熔点 | — | ASTM D-2133 | 175 | ℃ | ||
| 热传导系数 | — | — | 0.37 | W/mk | ||
| 线性热膨胀系数 | -40～29℃ | ASTM D-696 | 10.4 | 10m/m℃ | ||
| 线性热膨胀系数 | 29～60℃ | ASTM D-696 | 12.2 | 10m/m℃ | ||