PPO XYRON X1509

General
Material Status	Commercial: Active
Availability	Africa & Middle EastAsia PacificEuropeNorth America
Filler / Reinforcement	Filler, 10% Filler by Weight
Additive	Flame Retardant
Features	Flame RetardantHigh StiffnessLow Warpage
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density		g/cm3	ISO 1183
Molding Shrinkage 2 (0.0787 in)		%	Internal Method
Water Absorption (24 hr, 73°F)		%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield, 73°F)		psi	ISO 527
Tensile Strain (Break, 73°F)		%	ISO 527
Flexural Modulus (73°F)		psi	ISO 178
Flexural Stress (73°F)		psi	ISO 178
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength 3 (73°F)		ft·lb/in2	ISO 179
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
264 psi, Unannealed		°F	ISO 75-2
264 psi, Unannealed		°F	ASTM D648
CLTE			ISO 11359-2

PPO XYRON X1509

聚苯醚（PPO）中文名又叫聚苯醚b，是世界五大通用工程塑料之一。它具有刚性大、耐热性高、难燃，强度较高电性能优良等优点。另外，PPO还具有耐磨、无毒、耐污染等优点。PPO的介电常数和介电损耗在工程塑料中是最小的品种之一，几乎不受温度，湿度的影响。可用于低、中、高频电场领域（介电常数越小，绝缘性越好）PPO的负荷变形温度可达190℃以上，脱化温度-170℃。（PPO或PPE）又称聚亚苯基氧，化学名称为聚2,6-二甲基-1,4-苯醚。是2,6-二甲基苯酚通氧并在催化剂的作用下进行氧化缩合反应而成的线型聚合物。

PPO成型性能

1.非结晶料,吸湿小。

2.流动性差，为类似牛顿流体，粘度对温度比较敏感，制品厚度一般在0.8毫米以上。极易分解，分解时产生腐蚀气体。宜严格控制成型温度，模具应加热，浇注系统对料流阻力应小。

3、聚苯醚的吸水率很低0.06%左右，但微量的水分会导致产品表面出现银丝等不光滑现象，最好是作干燥处理，温度不可高出150度，否则颜色会变化。

4、聚苯醚的成型温度为280-330度，改性聚苯醚的成型温度为260-285度。

用途

1、电子电器工业上广泛用于制造连接器、线圈绕线轴、机械部件护罩、开关继电器、调谐设备、大型电子显示器、可变电容器、蓄电池配件、话筒等零部件。

2、家用电器上用于电视机、摄影机、录象带、录音机、空调机、加温器、电饭煲等零部件。可作复印机、计算机系统，打印机、传真机等外装件和组件。

3、另外可做照相机、计时器、水泵、鼓风机的外壳和零部件、无声齿轮、管道、阀体、外科手术器具、消毒器等医疗器具零部件。

4、大型吹塑成型可做汽车大型部件如阻流板、保险杠、低发泡成型适宜制作高刚性、尺寸稳定性、优良吸音性、内部结构复杂的大型制品，如各种机器外壳、底座、内部支架、设计自由度大，制品轻量化。

PPO XYRON X1509 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！