Lupoy? GN5001RFM

Technical Datasheet | Supplied by LG Chem

Lupoy? GN5001RFM is a general purpose, halogen-free flame retardant polycarbonate and acrylonitrile butadiene styrene (PC/ ABS) alloy by LG Chem. Exhibits high performance. Lupoy? GN5001RFM is suitable for processing by injection molding. Used in electric and electronic housings. Complies with UL 94 V0 flame rating.

Physical Properties物理性质	Metric公制数据	English英制数据	Comments测试方法
Specific Gravity 密度	1.18 g/cc	1.18 g/cc	ASTM D792
Maximum Moisture Content 最大水分含量	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow 线性收缩率/流动	0.0040 - 0.0060 cm/cm @Thickness 3.20 mm	0.0040 - 0.0060 in/in @Thickness 0.126 in	ASTM D955
Melt Flow 熔体流动速率	9.5 g/10 min @Load 2.16 kg, Temperature 250 °C	9.5 g/10 min @Load 4.76 lb, Temperature 482 °F	ASTM D1238
Mechanical Properties力学性能	Metric公制数据	English英制数据	Comments测试方法
Tensile Strength, Yield 屈服拉伸强度	54.9 MPa @Thickness 3.20 mm	7970 psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break 断裂伸长率	>= 50 % @Thickness 3.20 mm	>= 50 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength 弯曲屈服强度	86.3 MPa @Thickness 3.20 mm	12500 psi @Thickness 0.126 in	10mm/min; ASTM D790

PC/ABS LUPOY GN5001RFM

简介

ABS工程塑料即PC+ABS（工程塑料合金），在化工业的中文名字叫塑料合金，之所以命名为PC+ABS，是因为这种材料既具有PC树脂的优良耐热耐候性、尺寸稳定性和耐冲击性能，又具有ABS树脂优良的加工流动性。所以应用在薄壁及复杂形状制品，能保持其优异的性能，以及保持塑料与一种酯组成的材料的成型性。ABS工程塑料最大的缺点就是质量重、导热性能欠佳。它的成型温度取于它们两者原料的之间温度，就是240-265度，温度太高ABS会分解，太低PC料的流动性不良。

PC/ABS应用

1.汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件

2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器

3.电信，移动电话外壳，附件以及智能卡（SIM卡）：

4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道

5.家用电器，如洗衣机，吹风机，微波炉内外部件

PC/ABS注塑模工艺条件:

干燥处理：加工前的干燥处理是必须的。湿度应小于0.04%，建议干燥条件为90~110C，2~4小时。

熔化温度： 230~300C。

模具温度：50~100C。

注射压力：取决于塑件。

注射速度：尽可能地高。

PC/ABS LUPOY GN5001RFM 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！