VALOX 420SE0 PBT 沙伯基础（原美国GE)的产品特征：
加剂：30%玻纤增强
特点：阻燃
用途：开关 连接器
形式：微丸
处理方法：注塑成型
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Density | 1.63 g/cc | 0.0589 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.090 % | 0.090 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0050 cm/cm | 0.0010 - 0.0050 in/in | on Tensile Bar; SABIC Method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | on Tensile Bar; SABIC Method |
| 0.0050 - 0.010 cm/cm @Thickness 3.20 mm |
0.0050 - 0.010 in/in @Thickness 0.126 in |
SABIC Method | |
| Melt Flow | 42 g/10 min @Load 5.00 kg, Temperature 250 °C |
42 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 29 g/10 min @Load 5.00 kg, Temperature 250 °C |
29 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| 119 | 119 | ISO 2039-2 | |
| Hardness, H358/30 | 118 MPa | 17100 psi | ISO 2039-1 |
| Tensile Strength at Break | 120 MPa | 17400 psi | Type I, 5 mm/min; ASTM D638 |
| 120 MPa | 17400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 120 MPa | 17400 psi | Type I, 5 mm/min; ASTM D638 |
| 120 MPa | 17400 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1 mm/min; ISO 527 |
| 12.0 GPa | 1740 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| 186 MPa | 27000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 9.50 GPa | 1380 ksi | 2 mm/min; ISO 178 |
| 9.80 GPa | 1420 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| 0.570 J/cm @Temperature -30.0 °C |
1.07 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 6.20 J/cm | 11.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 6.00 kJ/m2 @Temperature -30.0 °C |
2.86 ft-lb/in2 @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m2 | 21.4 ft-lb/in2 | 80*10*4; ISO 180/1U |
| 45.0 kJ/m2 @Temperature -30.0 °C |
21.4 ft-lb/in2 @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 5.00 J/cm2 | 23.8 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 5.00 J/cm2 @Temperature -30.0 °C |
23.8 ft-lb/in2 @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.600 J/cm2 @Temperature -30.0 °C |
2.86 ft-lb/in2 @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 22 | 22 | CS-17, 1 kg; SABIC Method |
SABIC Innovative Plastics CYCOLOY C4220 PC ABS
SABIC Innovative Plastics CYCOLOY C6200 PC ABS
SABIC Innovative Plastics CYCOLOY C6600 PC ABS
SABIC Innovative Plastics CYCOLOY C6840 PC ABS
SABIC Innovative Plastics CYCOLOY C8080REC PC ABS
SABIC Innovative Plastics CYCOLOY CE1821 PC ABS
SABIC Innovative Plastics CYCOLOY CH6410 PC ABS
SABIC Innovative Plastics CYCOLOY CM6140 PC ABS
SABIC Innovative Plastics CYCOLOY CM6210 PC ABS
SABIC Innovative Plastics CYCOLOY CP8320 PC ABS
SABIC Innovative Plastics CYCOLOY CP8930 PC ABS
SABIC Innovative Plastics CYCOLOY CS9610 PC ABS
SABIC Innovative Plastics CYCOLOY CU1650 PC ABS
SABIC Innovative Plastics CYCOLOY CU6800 PC ABS
PBT树脂的Valox 树脂 半晶聚对苯二甲酸乙二醇酯，其中最广泛使用的工程材料之一，显示了低水分和热膨胀，并提供优秀的摩擦磨损性能。随着高温强度好，具有良好的电性能和阻燃性。
购买须知：
1、交易方式
新料最少起订量（MOQ）：一包（25KG。一般的报价都是含运费。.随货附上我司开具：送货单和收据。增值税发票一般是另外发快递。（顺丰和申通）。
2、付款方式
本公司接受现金交易，银行转账等等。其他需双方交涉之后决定。
3、配送方式
a、广东省内快递：我司默认“京广”，如果客户有指定快递公司的话，请在交易前和我们协商一致。广东省外，如客户需求也可以发快递，运费价格偏贵，一般是60-80元/袋。
b、广东省外物流：我司默认“德邦物流”“全峰”，款到当天发货（以发货物流单时间为准），如客户有协议的物流也可以自己指定。
c、外包装：所有物流和快递货物我司均免费添加一个外包装袋，以确保我们的货物在运输途中的安全。（减少破包。）
d、验货须知：客户接收货物时，有权对货物的型号，质量，数量，包装情况（烂包，破包）等进行确认。确认时请不要拆开原包装，以免发生不必要的损失。