LDPE BOREALIS PE CC7209
| Product Description | |
CC7209 is an extrusion coating grade especially designed for seal-peel applications. It gives smooth and easy peel when sealed against itself and PE. CC7209 provides also good adhesion to various substrates, particularly to aluminium. The rocommendation is to mix it with standard LDPE with the ratio 1:1 In this mixture processing like standard LDPE can be applied. The material must be pre-dried but there can be still a slight risk for filter blocking and filler agglomeration.
|
|
| General | |
Material Status |
|
Availability |
Africa & Middle EastAsia PacificEuropeLatin AmericaNorth America |
Filler / Reinforcement |
Filler, 30% Filler by WeightFiller |
Features |
Good AdhesionRecyclable Material |
Uses |
Coating ApplicationsFood PackagingLaminatesPackagingTie-Layer |
Processing Method |
|
LDPE BOREALIS PE CC7209
(1)乙烯聚合反应过程是一个强烈的放热过程。乙烯的聚合热约为93.5kJ/mol(或3.3kJ/g)，在235MPa、150~300℃下乙烯的比热容为2.51~2.85J/(g·℃)，反应热如果不能及时移去，每1%乙烯发生聚合将使温度升高12~13℃。如果温度过高，还会导致乙烯分解。
(2)在高压下，乙烯已被压缩到密度为0.5g/mL的气密相状态，近似于不能再压缩的液体，此时乙烯分子间的距离显著缩短，从而增加了游离基与乙烯分子的碰撞概率，所以容易发生聚合反应。
(3)高温下增长链的自由基活性大，容易发生链转移反应，所得到的聚合物为带有较多支链的线型结构。通常每1000个碳链原子中含有20~30个支链，结晶度为45%~65%，密度在0.910~0.925g/mL，质轻、具柔性，耐低温性、耐冲击性较好。
LDPE产品性能
低密度聚乙烯其特征主要有以下几点：
(1)薄膜呈微乳白透明色，柔软。强度比高密度聚乙烯小，抗冲击强度则比高密度聚乙烯大。
(2)耐寒、耐低温及耐较高温度。较厚的薄膜能承受90℃热水浸泡的杀菌过程。
(3)防潮性能比较好，化学性能稳定，不溶于一般溶剂。
(4)有较大的透气性，故用作易氧化的食品包装时，其内容物的贮存期不宜过长。
(5)耐油脂性较差，制品能被缓慢溶涨。包装含油脂食品时，久贮后会使食品出现哈喇味。
(6)长时期受紫外线及热作用会老化，影响其物理性能和介电性能。
(7)熔点为110~115℃，加工温度为150~210℃，若在惰性气体中，温度可达300℃仍稳定。但熔体和氧接触易发生降解作用。