TPE VERSAFLEX CL30
Versaflex? CL30 是一种容易加工的复合材料，设计用于要求具有极高透明度和极佳着色特性的注射模塑和挤出成型应用。
透明度极高
着色性极佳
可以重叠模塑方式粘接在聚丙烯上
手感柔软
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.888 g/cc | 0.888 g/cc | ASTM D792 |
| Viscosity | 14800 cP
|
14800 cP
|
ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.021 - 0.025 cm/cm | 0.021 - 0.025 in/in | ASTM D955 |
| Melt Flow | 18 g/10 min
|
18 g/10 min
|
ASTM D1238 |
| 110 g/10 min
|
110 g/10 min
|
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 30 | 30 | 10 sec; ASTM D2240 |
| Tensile Strength at Break | 5.18 MPa
|
751 psi
|
Die C2 hr; ASTM D412 |
| Tensile Stress | 0.689 MPa
|
99.9 psi
|
Die C2 hr; ASTM D412 |
| 1.38 MPa
|
200 psi
|
Die C2 hr; ASTM D412 | |
| Elongation at Break | 870 %
|
870 %
|
Die C2 hr; ASTM D412 |
| Tear Strength | 19.3 kN/m | 110 pli | ASTM D624 |
| Compression Set | 11 %
|
11 %
|
ASTM D395B |
TPE是一种具有橡胶的高弹性，高强度，高回弹性，又具有可注塑加工的特征，具有环保无毒安全，硬度范围广，有优良的着色性，触感柔软，耐候性，抗疲劳性和耐温性，加工性能优越，无须硫化，可以循环使用降低成本，既可以二次注塑成型，与PP、PE、PC、PS、ABS等基体材料包覆粘合，也可以单独成型。
优点：
一、易于回收利用，降低成本。生产过程中产生的废料和最终出现的废品，可以直接返回再利用；用过的TPE旧品可以简单再生之后回收利用，减少环境污染，扩大再生资源来源。
二、节能：热塑性弹性体大多不需要硫化或硫化时间很短，可以有效节约能源。
三、可用一般的热塑性塑料成型机加工，不需要特殊的加工设备。
四、生产效率大幅提高。可直接用橡胶注塑机硫化，时间由原来的20min左右，缩短到1min以内；由于需要的硫化时间很短，因此已可用挤出机直接硫化，生产效率大幅提高。
特点:
1.可用一般的热塑性塑料成型机加工，不需要特殊的加工设备。
2. 生产效率大幅提高。可直接用橡胶注塑机硫化，时间由原来的20min左右，缩短到1min以内；由于需要的硫化时间很短，因此已可用挤出机直接硫化，生产效率大幅提高。
3. 易于回收利用，降低成本。生产过程中产生的废料（逸出毛边、挤出废胶）和最终出现的废品，可以直接返回再利用；用过的TPE旧品可以简单再生之后回收利用，减少环境污染，扩大再生资源来源。
4. 节能。热塑性弹性体大多不需要硫化或硫化时间很短，可以有效节约能源。以高压软管生产能耗为例：橡胶为188MJ/kg，TPE为144MJ/kg，可节能达25%以上。
5. 应用领域更广。由于TPE兼具橡胶和塑料的优点，为橡胶工业开辟了新的应用领域。
6. 可用于塑料的增强、增韧改性。自补强性大，配方简化，配合剂对聚合物的影响制约小，质量性能更易掌握。但TPE的耐热性不如橡胶，随着温度上升而物性下降幅度较大，因而适用范围受到限制。同时，压缩变形、弹性回复、耐久性等同橡胶相比较差，价格上也往往高于同类橡胶。尽管如此，TPE的优点仍十分突出，各种新型的TPE产品也不断开发出来。作为一种节能环保的橡胶新型原料，发展前景十分看好。