TPE VERSAFLEX CL2250

General
Material Status	Commercial: Active
Availability	Africa & Middle EastAsia PacificLatin AmericaNorth America
Features	Good ColorabilityGood MoldabilityGood ProcessabilityGood Processing StabilityHigh Clarity
Uses	Medical/Healthcare ApplicationsOvermoldingPacifiersPersonal CareTransparent or Translucent Parts
Agency Ratings	1 2
RoHS Compliance
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density / Specific Gravity			ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)		g/10 min	ASTM D1238
Molding Shrinkage - Flow		in/in	ASTM D955
Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus		psi	ASTM D790
Elastomers	Nominal Value	Unit	Test Method
Tensile Stress 4, 5			ASTM D412
100% Strain, 73°F		psi
300% Strain, 73°F		psi
Tensile Strength 4, 5 (Break, 73°F)		psi	ASTM D412
Tensile Elongation 4, 5 (Break, 73°F)		%	ASTM D412
Tear Strength		lbf/in	ASTM D624
Compression Set (73°F, 22 hr)		%	ASTM D395B

TPE VERSAFLEX CL2250 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！

TPE是一种具有橡胶的高弹性，高强度，高回弹性，又具有可注塑加工的特征，具有环保无毒安全，硬度范围广，有优良的着色性，触感柔软，耐候性，抗疲劳性和耐温性，加工性能优越，无须硫化，可以循环使用降低成本，既可以二次注塑成型，与PP、PE、PC、PS、ABS等基体材料包覆粘合，也可以单独成型。

优点：

一、易于回收利用，降低成本。生产过程中产生的废料和最终出现的废品，可以直接返回再利用；用过的TPE旧品可以简单再生之后回收利用，减少环境污染，扩大再生资源来源。

二、节能：热塑性弹性体大多不需要硫化或硫化时间很短，可以有效节约能源。

三、可用一般的热塑性塑料成型机加工，不需要特殊的加工设备。

四、生产效率大幅提高。可直接用橡胶注塑机硫化，时间由原来的20min左右，缩短到1min以内；由于需要的硫化时间很短，因此已可用挤出机直接硫化，生产效率大幅提高。

特点:

1.可用一般的热塑性塑料成型机加工，不需要特殊的加工设备。

2. 生产效率大幅提高。可直接用橡胶注塑机硫化，时间由原来的20min左右，缩短到1min以内；由于需要的硫化时间很短，因此已可用挤出机直接硫化，生产效率大幅提高。

3. 易于回收利用，降低成本。生产过程中产生的废料（逸出毛边、挤出废胶）和最终出现的废品，可以直接返回再利用；用过的TPE旧品可以简单再生之后回收利用，减少环境污染，扩大再生资源来源。

4. 节能。热塑性弹性体大多不需要硫化或硫化时间很短，可以有效节约能源。以高压软管生产能耗为例：橡胶为188MJ/kg，TPE为144MJ/kg，可节能达25%以上。

5. 应用领域更广。由于TPE兼具橡胶和塑料的优点，为橡胶工业开辟了新的应用领域。

6. 可用于塑料的增强、增韧改性。自补强性大，配方简化，配合剂对聚合物的影响制约小，质量性能更易掌握。但TPE的耐热性不如橡胶，随着温度上升而物性下降幅度较大，因而适用范围受到限制。同时，压缩变形、弹性回复、耐久性等同橡胶相比较差，价格上也往往高于同类橡胶。尽管如此，TPE的优点仍十分突出，各种新型的TPE产品也不断开发出来。作为一种节能环保的橡胶新型原料，发展前景十分看好。