ABS NOVODUR H702 

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in3	ISO 1183
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ISO 294-4
Melt Flow	16 g/10 min @Load 10.0 kg, Temperature 220 °C	16 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133
Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	105 MPa	15200 psi	ISO 2039-1
Tensile Strength, Yield	46.0 MPa	6670 psi	ISO 527
Elongation at Break	15 %	15 %	ISO 527
Elongation at Yield	2.6 %	2.6 %	ISO 527
Tensile Modulus	2.50 GPa	363 ksi	ISO 527
Flexural Strength	73.0 MPa	10600 psi	ISO 178
Flexural Modulus	2.40 GPa	348 ksi	ISO 178
Izod Impact, Notched (ISO)	8.00 kJ/m2 @Temperature -30.0 °C	3.81 ft-lb/in2 @Temperature -22.0 °F	ISO 180/A
	17.0 kJ/m2 @Temperature 23.0 °C	8.09 ft-lb/in2 @Temperature 73.4 °F	ISO 180/A
Charpy Impact Unnotched	9.00 J/cm2 @Temperature -30.0 °C	42.8 ft-lb/in2 @Temperature -22.0 °F	ISO 179
	10.0 J/cm2 @Temperature 23.0 °C	47.6 ft-lb/in2 @Temperature 73.4 °F	ISO 179

ABS NOVODUR H702 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！

成型性能

无定形材料,流动性中等,吸湿大,必须充分干燥,表面要求光泽的塑件须长时间预热干燥80-90度,3小时；

宜取高料温,高模温,但料温过高易分解(分解温度为>270度).对精度较高的塑件,模温宜取50-60度,对高光泽.耐热塑件,模温宜取60-80度；

如需解决夹水纹，需提高材料的流动性，采取高料温、高模温，或者改变入水位等方法；

如成形耐热级或阻燃级材料，生产3-7天后模具表面会残存塑料分解物，导致模具表面发亮，需对模具及时进行清理，同时模具表面需增加排气位置；

冷却速度快，模具浇注系统应以粗，短为原则，宜设冷料穴，浇口宜取大，如：直接浇口，圆盘浇口或扇形浇口等，但应防止内应力增大，必要时可采用调整式浇口。模具宜加热，应选用耐磨钢； 

料温对塑件质量影响较大，料温过低会造成缺料，表面无光泽，银丝紊乱料温过高易溢边，出现银丝暗条，塑件变色起泡；

用途

ABS树脂的最大应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。