Product Description
SABIC® LDPE 2308N0 is a LDPE tubular grade without additives. SABIC® LDPE 2308N0 is produced using SABIC Clean Tubular Reactor (CTR) Technology. Application SABIC® LDPE 2308N0 is typically used as carrier resin for masterbatch and compounding applications. This product is not intended for and must not be used in any pharmaceutical/medical applications.
General
Material Status	Commercial: Active
Availability	Africa & Middle EastAsia PacificEuropeLatin AmericaNorth America
Uses	Industrial Applications

Physical	Nominal Value	Unit	Test Method
Density		g/cm3	ASTM D1505
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg		g/10 min
190°C/5.0 kg		g/10 min
Melt Volume-Flow Rate (MVR)			ISO 1133
190°C/2.16 kg		cm3/10min
190°C/5.0 kg		cm3/10min
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus		psi	ISO 527-2/1A/50
Tensile Stress			ISO 527-2/1A/50
Yield		psi
Break		psi
Tensile Strain (Break)		%	ISO 527-2/1A/50

LDPE SABIC 2308N0

(1)乙烯聚合反应过程是一个强烈的放热过程。乙烯的聚合热约为93.5kJ/mol(或3.3kJ/g)，在235MPa、150~300℃下乙烯的比热容为2.51~2.85J/(g·℃)，反应热如果不能及时移去，每1%乙烯发生聚合将使温度升高12~13℃。如果温度过高，还会导致乙烯分解。

(2)在高压下，乙烯已被压缩到密度为0.5g/mL的气密相状态，近似于不能再压缩的液体，此时乙烯分子间的距离显著缩短，从而增加了游离基与乙烯分子的碰撞概率，所以容易发生聚合反应。

(3)高温下增长链的自由基活性大，容易发生链转移反应，所得到的聚合物为带有较多支链的线型结构。通常每1000个碳链原子中含有20~30个支链，结晶度为45%~65%，密度在0.910~0.925g/mL，质轻、具柔性，耐低温性、耐冲击性较好。

LDPE产品性能

低密度聚乙烯其特征主要有以下几点：

(1)薄膜呈微乳白透明色，柔软。强度比高密度聚乙烯小，抗冲击强度则比高密度聚乙烯大。

(2)耐寒、耐低温及耐较高温度。较厚的薄膜能承受90℃热水浸泡的杀菌过程。

(3)防潮性能比较好，化学性能稳定，不溶于一般溶剂。

(4)有较大的透气性，故用作易氧化的食品包装时，其内容物的贮存期不宜过长。

(5)耐油脂性较差，制品能被缓慢溶涨。包装含油脂食品时，久贮后会使食品出现哈喇味。

(6)长时期受紫外线及热作用会老化，影响其物理性能和介电性能。

(7)熔点为110~115℃，加工温度为150~210℃，若在惰性气体中，温度可达300℃仍稳定。但熔体和氧接触易发生降解作用。

LDPE应用领域

低密度聚乙烯的应用范围:适用于调味料、糕点、糖、蜜饯、饼干、奶粉、茶叶、鱼肉松等食品包装。片剂、粉剂等药品包装,衬衫、服装、针织棉制品及化纤制品等纤维制品包装。洗衣粉、洗涤剂、化妆品等日化用品包装。由于单层PE薄膜的机械性能较差,所以通常用作复合包装袋的内层,即多层复合薄膜热封性基材。

LDPE SABIC 2308N0 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！