SABIC® LDPE 2102X0 by SABIC is a non-additivated & non-stabilized low density polyethylene (LDPE) grade. Is produced using SABIC's proprietary high pressure Clean Tubular Reactor (CTR®) technology. Exhibits very high cleanliness and consistent purity. Designed for wire and cable extrusion applications. SABIC® LDPE 2102X0 is recommended for the production of medium/ high voltage power cable insulation using the direct peroxide addition.
物理性能 | 额定值 |
单位制 |
测试方法 |
密度 |
g/cm3 |
ASTM D1505 | |
熔流率(熔体流动速率) (190°C/2.16 kg) |
g/10 min |
ISO 1133 | |
机械性能 | 额定值 |
单位制 |
测试方法 |
拉伸模量 |
|||
-- |
psi |
ISO 527-2 | |
-- |
psi |
内部方法 | |
拉伸应力 |
ISO 527-2 | ||
屈服 |
psi |
||
断裂 |
psi |
||
拉伸应变 (断裂) |
% |
ISO 527-2 | |
硬度 | 额定值 |
单位制 |
测试方法 |
肖氏硬度 (邵氏 D) |
ISO 868 | ||
热性能 | 额定值 |
单位制 |
测试方法 |
维卡软化温度 |
°F |
ISO 306/A | |
熔融温度 |
°F |
DIN 53765 | |
Average Heat of Fusion |
J/g |
DIN 53765 | |
Crystallization Temperature |
°F |
DIN 53765 |
LDPE SABIC 2102X0
(1)乙烯聚合反应过程是一个强烈的放热过程。乙烯的聚合热约为93.5kJ/mol(或3.3kJ/g),在235MPa、150~300℃下乙烯的比热容为2.51~2.85J/(g·℃),反应热如果不能及时移去,每1%乙烯发生聚合将使温度升高12~13℃。如果温度过高,还会导致乙烯分解。
(2)在高压下,乙烯已被压缩到密度为0.5g/mL的气密相状态,近似于不能再压缩的液体,此时乙烯分子间的距离显著缩短,从而增加了游离基与乙烯分子的碰撞概率,所以容易发生聚合反应。
(3)高温下增长链的自由基活性大,容易发生链转移反应,所得到的聚合物为带有较多支链的线型结构。通常每1000个碳链原子中含有20~30个支链,结晶度为45%~65%,密度在0.910~0.925g/mL,质轻、具柔性,耐低温性、耐冲击性较好。
LDPE产品性能
低密度聚乙烯其特征主要有以下几点:
(1)薄膜呈微乳白透明色,柔软。强度比高密度聚乙烯小,抗冲击强度则比高密度聚乙烯大。
(2)耐寒、耐低温及耐较高温度。较厚的薄膜能承受90℃热水浸泡的杀菌过程。
(3)防潮性能比较好,化学性能稳定,不溶于一般溶剂。
(4)有较大的透气性,故用作易氧化的食品包装时,其内容物的贮存期不宜过长。
(5)耐油脂性较差,制品能被缓慢溶涨。包装含油脂食品时,久贮后会使食品出现哈喇味。
(6)长时期受紫外线及热作用会老化,影响其物理性能和介电性能。
(7)熔点为110~115℃,加工温度为150~210℃,若在惰性气体中,温度可达300℃仍稳定。但熔体和氧接触易发生降解作用。
LDPE应用领域
低密度聚乙烯的应用范围:适用于调味料、糕点、糖、蜜饯、饼干、奶粉、茶叶、鱼肉松等食品包装。片剂、粉剂等药品包装,衬衫、服装、针织棉制品及化纤制品等纤维制品包装。洗衣粉、洗涤剂、化妆品等日化用品包装。由于单层PE薄膜的机械性能较差,所以通常用作复合包装袋的内层,即多层复合薄膜热封性基材。