EL-Lene™ F15
Technical Datasheet | Supplied by SCG Chemicals
EL-Lene™ F15 by SCG Chemicals is a recyclable high density polyethylene (HDPE) grade. It is a product of bi-modal process from Mitsui Chemicals, Inc. of Japan. Exhibits high productivity, high tensile strength with good dart impact strength, good moisture barrier, low gel content and excellent printing properties. EL-Lene™ F15 is insoluble in water and suitable for processing by blown film extrusion. Recommended for shopping bag, T-shirt bag, garbage bag and linear bag. Complies with U.S FDA 21 CFR 177.1520.
| 物理性能 | 额定值 |
单位制 |
测试方法 |
密度 |
g/cm3 |
ASTM D1505 | |
熔流率（熔体流动速率） (190°C/2.16 kg) |
g/10 min |
ASTM D1238 | |
抗环境应力开裂 (122°F, 25% Igepal, 模压成型, F50) |
hr |
ASTM D1693B | |
| 薄膜 | 额定值 |
单位制 |
测试方法 |
割线模量 |
ASTM D882 | ||
2% 正割, MD : 0.47 mil |
psi |
||
2% 正割, TD : 0.47 mil |
psi |
||
抗张强度 |
ASTM D882 | ||
TD : 屈服, 0.47 mil |
psi |
||
MD : 断裂, 0.47 mil |
psi |
||
TD : 断裂, 0.47 mil |
psi |
||
伸长率 |
ASTM D882 | ||
MD : 断裂, 0.47 mil |
% |
||
TD : 断裂, 0.47 mil |
% |
||
落锤冲击 (0.47 mil) |
g |
ASTM D1709 | |
埃尔曼多夫抗撕强度 |
ASTM D1922 |
HDPE EL-LENE F15
基本特性：高密度聚乙烯是一种不透明白色腊状材料，比重比水轻，比重为0.941~0.960，柔软而且有韧性，但比LDPE略硬，也略能伸长，无毒，无味。
燃烧特性：易燃，离火后能继续燃烧，火焰上端呈黄色，下端呈蓝色，燃烧时会熔融，有液体滴落，无黑烟冒出，同时，发出石蜡燃烧时发出的气味。
主要优点：耐酸碱，耐有机溶剂，电绝缘性优良，低温时，仍能保持一定的韧性。表面硬度，拉伸强度，刚性等机械强度都高于LDPE，接近于PP，比PP韧，但表面光洁度不如PP。
主要缺点：机械性能差，透气差，易变形，易老化，易发脆，脆性低于PP，易应力开裂，表面硬度低，易刮伤。难印刷，印刷时，需进行表面放电处理，不能电镀，表面无光泽。
主要用途：
高密度聚乙烯树脂可采用注射、挤出、吹塑和旋转成型等方法成型塑料制品。采用注射成型可成型出各种类型的容器、工业配件、医用品、玩具、壳体、瓶塞和护罩等制品。采用吹塑成型可成型各种中空容器、超薄型薄膜等。采用挤出成型可成型管材、拉伸条带、捆扎带、单丝、电线和电缆护套等。
另外，还可成型建筑用装饰板、百叶窗、合成木材、合成纸、合成膜和成型钙塑制品等 。