LCP VECTRA  1.jpg

LCP VECTRA A435

Physical Properties Metric English Comments
Density  1.62 g/cc 0.0585 lb/in3 ISO 1183
Moisture Absorption  0.00200 % 0.00200 % 23°C/50%RH; ISO 62
Linear Mold Shrinkage, Flow  0.0010 cm/cm 0.0010 in/in ISO 294-4
Linear Mold Shrinkage, Transverse  0.0040 cm/cm 0.0040 in/in ISO 294-4

Mechanical Properties Metric English Comments
Hardness, Rockwell M  55 55 ISO 2039-2
Tensile Strength at Break  171 MPa 24800 psi 5mm/min; ISO 527-2/1A
Elongation at Break  3.3 % 3.3 % 5mm/min; ISO 527-2/1A
Tensile Modulus  11.0 GPa 1600 ksi 50mm/min; ISO 527-2/1A
Flexural Strength  206 MPa 29900 psi ISO 178
Flexural Modulus  10.5 GPa 1520 ksi ISO 178
Compressive Strength  77.0 MPa
@Strain 1.00 %
11200 psi
@Strain 1.00 %
ISO 604
Compressive Modulus  10.5 GPa 1520 ksi ISO 604
Izod Impact, Notched (ISO)  17.0 kJ/m2 8.09 ft-lb/in2 ISO 180/1A
  33.0 kJ/m2
@Temperature 23.0 °C
15.7 ft-lb/in2
@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched  3.80 J/cm2 18.1 ft-lb/in2 ISO 179/1eU
Charpy Impact, Notched  2.60 J/cm2 12.4 ft-lb/in2 ISO 179/1eA

LCP VECTRA A435

主要性能

1.高温电气/电子装配:能承受SMT装配工序操作,包括无铅回流焊接。2.卓越的热老化性能,在高温下保持固有特性。

3.卓越的流动性-薄壁,复杂的形状。

4.尺寸稳定性极佳,模塑收缩率低,热膨胀系数极小,可与金属相媲美。

5.在成型时,分子链朝着流动的方向排列,产生一种好似其分子自身将其增强的自增强效果。

6.可获得极高的强和弹性模量。

7.优异的耐化学腐蚀性。

8.模塑速度:周期循环极快。

9.卓越的抗蠕变性。

10.阻燃性。

11.在宽广的温度范围内具有卓越的介电性能。


LCP的主要应用领域:

连接器系列、BOBBIN、接插件、SIMM插口、LED(MID)、QFP插口、微波炉支架、热风筒、烫发器、注射成型线路部件(MID)、光感应器(MID)、水晶振荡器座(MID)、集成块支承座、耳机部件、光缆拉伸件、光缆连接器、光缆接插器、针式打印机的线圈、针式打印机的底座、电扇、照相机快门板、泵的部件、USB系列、CD拾音器部件、印刷电路板、线圈骨架的封装材、作光纤电缆接头护套和高强度元件喷气发动机零件等电子电器。.

LCP VECTRA A435 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料,价格最优,质量保证!

首页 橡塑 / 工程塑料 / 液晶聚合物(LCP)
相关产品
店内推荐
首页
店铺
拨打电话 立即报价
发送询价单
采购商品:
采购数量:
联系信息:
公司名称:
采购说明:
 
您的询盘第一时间将不发送给其他供应商,但该供应商24 小时未响应情况下,仍将为您分配更合适供应商
图形验证:
图形验证码 换一换
验证码校验