Lupoy® GN5008HF

Technical Datasheet | Supplied by LG Chem

Lupoy® GN5008HF is a high flow, halogen-free flame retardant polycarbonate and acrylonitrile butadiene styrene (PC/ ABS) alloy by LG Chem. Exhibits high performance and high impact resistance. Lupoy® GN5008HF is suitable for processing by injection molding. Used in OA and navigation housings. Complies with UL 94 V0 flame rating.

LG Chemical LUPOY GN5008HF Halogen Free PC/ABS The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
Physical Properties物理性质	Metric公制数据	English英制数据	Comments测试方法
Specific Gravity 密度	1.18 g/cc	1.18 g/cc	ASTM D792
Linear Mold Shrinkage 线性收缩率	0.0040 cm/cm	0.0040 in/in	ASTM D955
Linear Mold Shrinkage, Transverse 线性收缩率/横向断裂拉伸强度	0.0060 cm/cm	0.0060 in/in	ASTM D955
Melt Flow 熔体流动速率	30 g/10 min @Load 2.16 kg, Temperature 250 °C	30 g/10 min @Load 4.76 lb, Temperature 482 °F
Mechanical Properties力学性能	Metric公制数据	English英制数据	Comments测试方法
Hardness, Rockwell罗氏硬度 R	113	113	ASTM D785
Tensile Strength, Yield 屈服拉伸强度	58.0 MPa	8410 psi	ASTM D638
Elongation at Break 断裂伸长率	50 %	50 %	ASTM D638
Flexural Strength 弯曲强度	83.0 MPa	12000 psi	ASTM D790

PC/ABS LUPOY GN5008HF 

简介

ABS工程塑料即PC+ABS（工程塑料合金），在化工业的中文名字叫塑料合金，之所以命名为PC+ABS，是因为这种材料既具有PC树脂的优良耐热耐候性、尺寸稳定性和耐冲击性能，又具有ABS树脂优良的加工流动性。所以应用在薄壁及复杂形状制品，能保持其优异的性能，以及保持塑料与一种酯组成的材料的成型性。ABS工程塑料最大的缺点就是质量重、导热性能欠佳。它的成型温度取于它们两者原料的之间温度，就是240-265度，温度太高ABS会分解，太低PC料的流动性不良。

PC/ABS应用

1.汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件

2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器

3.电信，移动电话外壳，附件以及智能卡（SIM卡）：

4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道

5.家用电器，如洗衣机，吹风机，微波炉内外部件

PC/ABS注塑模工艺条件:

干燥处理：加工前的干燥处理是必须的。湿度应小于0.04%，建议干燥条件为90~110C，2~4小时。

熔化温度： 230~300C。

模具温度：50~100C。

注射压力：取决于塑件。

注射速度：尽可能地高。

PC/ABS LUPOY GN5008HF 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！