东莞市众垒塑胶有限公司
.供应PMMA CM-205台湾奇美
特性备注：热型射出级、能耐高温、热变形温度高达100°C、机械性强耐。
用途：汽机车指示灯外壳、太阳眼镜片、电子表面外壳。
重要参数：熔体流动速率:1.8 g/10min密度:1.19 g/cm3吸水率:0.3 %成型收缩率:0.004 %拉伸强度:70 MPa
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
| 基本性能 |
硬度 |
|
ASTM D-785 |
M-95 |
|
| 假密度 |
|
ASTM D-1182 |
0.77 |
g/cm3 |
|
| 吸水率 |
|
ASTM D-570 |
0.3 |
% |
|
| 物理性能 |
比重 |
|
ASTM D-792 |
1.19 |
|
| 全光透过率 |
|
ASTM D-1003 |
92 |
% |
|
| 流动系数 |
|
ASTM D-1238 |
1.8 |
g/10min |
|
| 燃烧率 |
|
|
1/16"HB |
UL-94 |
|
| 成型收缩率 |
|
ASTM D-955 |
0.002-0.006 |
mm/mm |
|
| 机械性能 |
抗冲击力 |
|
ASTM D-256 |
2.0 |
kg-cm/cm |
| 引张强度 |
|
ASTM D-638/PSI |
10200/720 |
Kg/cm2 |
|
| 弯曲强度 |
|
ASTM D-790/PSI |
15600/1100 |
Kg/cm2 |
|
| 延伸率 |
|
ASTM D-638 |
5.0 |
% |
|
| 曲折率 |
|
ASTM D-542 |
1.491 |
|
|
| 绝缘耐力 |
|
ASTM D-149 |
500 |
Volts/Mil |
|
| 抗冲击力 |
|
ASTM D-256 |
0.37 |
ft-lbs/in2 |
|
| 电气性能 |
体积固有抵抗 |
|
ASTM D-257 |
1015 |
Ω.m |
| 失电率 |
|
ASTM D-150 |
0.19 |
|
|
| 诱电率 |
|
ASTM D-150-647b |
3.7 |
|
|
| 诱电率力 |
|
ASTM D-150-647 |
0.5 |
|
|
| 热性能 |
热变形温度 |
|
ASTM D-648 |
100/212 |
°C/°F |
| 维卡软化点 |
|
ASTM D-648 |
113/235 |
°C/°F |
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
| 基本性能 |
硬度 |
|
ASTM D-785 |
M-95 |
|
| 假密度 |
|
ASTM D-1182 |
0.77 |
g/cm3 |
|
| 吸水率 |
|
ASTM D-570 |
0.3 |
% |
|
| 物理性能 |
比重 |
|
ASTM D-792 |
1.19 |
|
| 全光透过率 |
|
ASTM D-1003 |
92 |
% |
|
| 流动系数 |
|
ASTM D-1238 |
1.8 |
g/10min |
|
| 燃烧率 |
|
|
1/16"HB |
UL-94 |
|
| 成型收缩率 |
|
ASTM D-955 |
0.002-0.006 |
mm/mm |
|
| 机械性能 |
抗冲击力 |
|
ASTM D-256 |
2.0 |
kg-cm/cm |
| 引张强度 |
|
ASTM D-638/PSI |
10200/720 |
Kg/cm2 |
|
| 弯曲强度 |
|
ASTM D-790/PSI |
15600/1100 |
Kg/cm2 |
|
| 延伸率 |
|
ASTM D-638 |
5.0 |
% |
|
| 曲折率 |
|
ASTM D-542 |
1.491 |
|
|
| 绝缘耐力 |
|
ASTM D-149 |
500 |
Volts/Mil |
|
| 抗冲击力 |
|
ASTM D-256 |
0.37 |
ft-lbs/in2 |
|
| 电气性能 |
体积固有抵抗 |
|
ASTM D-257 |
1015 |
Ω.m |
| 失电率 |
|
ASTM D-150 |
0.19 |
|
|
| 诱电率 |
|
ASTM D-150-647b |
3.7 |
|
|
| 诱电率力 |
|
ASTM D-150-647 |
0.5 |
|
|
| 热性能 |
热变形温度 |
|
ASTM D-648 |
100/212 |
°C/°F |
| 维卡软化点 |
|
ASTM D-648 |
113/235 |
°C/°F |
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
|
| 基本性能 |
硬度 |
|
ASTM D-785 |
M-95 |
|
| 假密度 |
|
ASTM D-1182 |
0.77 |
g/cm3 |
|
| 吸水率 |
|
ASTM D-570 |
0.3 |
% |
|
| 物理性能 |
比重 |
|
ASTM D-792 |
1.19 |
|
| 全光透过率 |
|
ASTM D-1003 |
92 |
% |
|
| 流动系数 |
|
ASTM D-1238 |
1.8 |
g/10min |
|
| 燃烧率 |
|
|
1/16"HB |
UL-94 |
|
| 成型收缩率 |
|
ASTM D-955 |
0.002-0.006 |
mm/mm |
|
| 机械性能 |
抗冲击力 |
|
ASTM D-256 |
2.0 |
kg-cm/cm |
| 引张强度 |
|
ASTM D-638/PSI |
10200/720 |
Kg/cm2 |
|
| 弯曲强度 |
|
ASTM D-790/PSI |
15600/1100 |
Kg/cm2 |
|
| 延伸率 |
|
ASTM D-638 |
5.0 |
% |
|
| 曲折率 |
|
ASTM D-542 |
1.491 |
|
|
| 绝缘耐力 |
|
ASTM D-149 |
500 |
Volts/Mil |
|
| 抗冲击力 |
|
ASTM D-256 |
0.37 |
ft-lbs/in2 |
|
| 电气性能 |
体积固有抵抗 |
|
ASTM D-257 |
1015 |
Ω.m |
| 失电率 |
|
ASTM D-150 |
0.19 |
|
|
| 诱电率 |
|
ASTM D-150-647b |
3.7 |
|
|
| 诱电率力 |
|
ASTM D-150-647 |
0.5 |
|
|
| 热性能 |
热变形温度 |
|
ASTM D-648 |
100/212 |
°C/°F |
| 维卡软化点 |
|
ASTM D-648 |
113/235 |
°C/°F |
1.供应PMMA CM-205台湾奇美 耐候性 高耐热 高强度
用途:保护性遮盖物.汽车领域的应用
2.供应PMMA CM-207台湾奇美 耐候性 高耐热 高强度 高光泽
用途:化妆品.汽车内部零件.旋钮.家用货品.容器.浴室配件
3.供应PMMA CM-211台湾奇美 高流动 耐候性 高耐热 高光泽
用途:化妆品.容器.家用货品.旋钮
4.供应PMMA 80N日本旭化成 高耐热 注塑级HDT=100℃
用途:汽车领域的应用
重要参数：熔体流动速率:2 g/10min密度:1.19 g/cm3吸水率:0.3 %成型收缩率:0.004 %缺口冲击强度:1.6
5.供应PMMA 560F日本旭化成 高流动 耐候性
特性备注：动性好，透明性，耐气候性、表面硬度及耐化学药品性优异
用途：适合形状复杂的制品，大型制品。
重要参数：熔体流动速率:13 g/10min密度:1.19 g/cm3吸水率:0.3 %成型收缩率:0.004 %缺口冲击强度:1.5
6.供应PMMA MF001日本三菱丽阳 高耐热 注塑级
特性备注：耐热
重要参数：熔体流动速率:2.5 g/10min密度:1.19 g/cm3吸水率:0.3 %成型收缩率:0.4 %缺口冲击强度:1.6
7).供应PMMA VRL-40日本三菱丽阳 易流动 高耐热 高抗冲
用途:管道.条材
8.供应PMMA韩国LG IF850
特性备注：流动性
用途：适用于复杂的架子或面积大而薄的墙饰件
重要参数：熔体流动速率:12.5 g/10min密度:1.18 g/cm3吸水率:0.3 %成型收缩率:0.4 %缺{口冲击强度:1.6
9).供应PMMA韩国LG IG840
重要参数：熔体流动速率:5.8 g/10min密度:1.18 g/cm3吸水率:0.3 %成型收缩率:0.4 %缺口冲击强度:1.6