INFINO® HN-1074

Technical Datasheet | Supplied by LOTTE Advanced Materials

INFINO® HN-1074 by LOTTE Advanced Materials is a halogen-free, flame retarded polycarbonate (PC) grade. Exhibits high impact strength, high modulus & flowability, good colorability, excellent appearance and well-balanced mechanical properties & processability. Can be processed using injection molding. INFINO® HN-1074 is recommended for home appliances.

PC INFINO HN-1074

General
Material Status	Commercial: Active
Availability	Africa & Middle EastAsia PacificEuropeLatin AmericaNorth America

Physical	Nominal Value	Unit	Test Method
Density / Specific Gravity
Natural			ASTM D792
Natural		g/cm3	ISO 1183
Melt Mass-Flow Rate (MFR) (250°C/10.0 kg)		g/10 min	ASTM D1238, ISO 1133
Molding Shrinkage
Flow : 0,126 in		in/in	ASTM D955
Across Flow : 0,126 in		in/in	ASTM D955
Across Flow : 0,0787 in		%	ISO 294-4
Flow : 0,0787 in		%	ISO 294-4
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
-- 2		psi	ASTM D638
--		psi	ISO 527-2/50
Tensile Strength
Yield 2		psi	ASTM D638
Yield		psi	ISO 527-2/50
Break 2		psi	ASTM D638
Break		psi	ISO 527-2/50

PC INFINO HN-1074 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！

塑料的处理

PC塑胶原料的吸水率较大，加工前一定要预热干燥，纯PC干燥120℃，改性PC一般用110℃温度干燥4小时以上。干燥时间不能超过10小时。一般可用对空挤出法判断干燥是否足够。再生料的使用比例可达20%。在某些情况下，可100%的使用再生料，实际份量要视制品的品质要求而定。再生料不能同时混合不同的色母粒，否则会严重损坏成品的性质。

注塑机选用

PC塑料制品由于成本及其它方面的原因，多用改性材料，特别是电工产品，还须增加防火性能，在阻燃的PC和其它塑料合金产品成型时，对注塑机塑化系统的要求是混合好、耐腐蚀，常规的塑化螺杆难以做到，在选购时，一定要预先说明。

主要优点

1．具高强度及弹性系数、高冲击强度、使用温度范围广；

2．高度透明性及自由染色性；

3．成形收缩率低、尺寸安定性良好；

4．耐疲劳性佳；

5．耐候性佳；

6．电气特性优。

性能特点:良好的流动性;脱模性能良好;

粘度，高；光学透明性好、抗冲击强度高；

并具有优异的热安稳性、耐蠕变性、抗寒性、电绝缘性和阻燃性等。

加工方法:薄膜挤出；吹塑成型；挤出成型；热成型；树脂传递成型；涂层；砑光；注射成型也是最重要的加工方法之一；

用途:在透明建筑板材、电子电器、光盘、汽车工业、机械、光学、医药等领域得到广泛运用。

PC塑料物理性能以及加工

低温-45度聚碳酸酯无色透明，耐热，抗冲击，阻燃BI级，在普通运用温度内都有出色的机械功用。