LEXAN™ Resin FXG1413T
Technical Datasheet | Supplied by SABIC
LEXAN™ Resin FXG1413T is an amorphous PC-siloxane copolymer with ‘diamond sparkle’ appearance. Is a medium flow grade with improved toughness compared to medium flow standard PC. Possesses high mechanical, optical, electrical and thermal properties. Provides molded-in effects eliminating the need of after molding modifications and offers cleaner and long-lasting part aesthetics. Exhibits impact resistance, clarity and outstanding dimensional stability. Processed by injection molding.
Lexan PC FXG1413T物性
物理性能 | 额定值 |
单位制 |
测试方法 |
比重 |
1.18 |
g/cm3 |
ASTM D792, ISO 1183 |
熔流率 (300°C/1.2 kg) |
10 |
g/10 min |
ASTM D1238 |
溶化体积流率(MVR) (300°C/1.2 kg) |
9.40 |
cm3/10min |
ISO 1133 |
收缩率 |
内部方法 | ||
流动 3 |
0.40 到 0.80 |
% |
|
流动 : 3.20 mm |
0.40 到 0.80 |
% |
|
横向流动 : 3.20 mm |
0.40 到 0.80 |
% |
|
吸水率 |
ISO 62 | ||
饱和, 23°C |
0.12 |
% |
|
平衡, 23°C, 50% RH |
0.090 |
% |
机械性能 | 额定值 |
单位制 |
测试方法 |
拉伸模量 |
|||
-- 4 |
2270 |
MPa |
ASTM D638 |
-- |
2330 |
MPa |
ISO 527-2/1 |
抗张强度 |
|||
屈服 5 |
59.0 |
MPa |
ASTM D638 |
屈服 |
57.0 |
MPa |
ISO 527-2/50 |
断裂 5 |
47.0 |
MPa |
ASTM D638 |
断裂 |
46.0 |
MPa |
ISO 527-2/50 |
PC LEXAN FXG1413T 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料,价格最优,质量保证!
特性:
为非结晶性热塑性塑料,优质的耐热性能、良好的透明度和极高的耐冲击强度等物理机械性能。
优点:
1.具高强度及弹性系数、高冲击强度、使用温度范围广;
2.高度透明性及自由染色性;
3.H.D.T.高;
4.耐疲劳性差;
5、耐候性佳;
6.电气特性优;
7.无味无臭对人体无害符合卫生安全;
8.成形收缩率低、尺寸安定性良好。
应用
PC工程塑料的三大应用领域是玻璃装配业、汽车工业和电子、电器工业,其次还有工业机械零件、光盘、包装、计算机等办公室设备、医疗及保健、薄膜、休闲和防护器材等。PC可用作门窗玻璃,PC层压板广泛用于银行、使馆、拘留所和公共场所的防护窗,用于飞机舱罩,照明设备、工业安全档板和防弹玻璃。
汽车制造业
聚碳酸酯具有良好的抗冲击、抗热畸变性能,而且耐候性好、硬度高,因此适用于生产轿车和轻型卡车的各种零部件,其主要集中在照明系统、仪表板、加热板、除霜器及聚碳酸酯合金制的保险杠等。
建材行业
聚碳酸酯板材具有良好的透光性,抗冲击性,耐紫外线辐射及其制品的尺寸稳定性和良好的成型加工性能,使其比建筑业传统使用的无机玻璃具有明显的技术性能优势。中国建有聚碳酸酯建材中空板生产线20余条,年需用聚碳酸酯7万吨左右,到2005年达到14万吨。