CYCOLOY™ Resin CE1821

Technical Datasheet | Supplied by SABIC

Discontinued : product no longer available

CYCOLOY™ Resin CE1821 is a filled blend of Polycarbonate and Acrylonitrile-butadiene-styrene (ABS). Is amorphous, durable and possesses high stiffness. Offers outstanding dimensional stability and high modulus with superior ductility. Exhibits low coefficient of thermal expansion, high impact and heat resistance. Provides a high quality surface suitable for painting along with good processability. Used for extrusion and thermoforming applications.

PC+ABS CYCOLOY CE1821

物理性能	额定值	单位制	测试方法
比重	1.22	g/cm3	ASTM D792, ISO 1183
熔流率 (260°C/5.0 kg)	12	g/10 min	ASTM D1238
溶化体积流率（MVR） (260°C/5.0 kg)	10.0	cm3/10min	ISO 1133
收缩率 - 流动 (3.20 mm)	0.50 到 0.70	%	内部方法
吸水率			ISO 62
饱和, 23°C	0.40	%
平衡, 23°C, 50% RH	0.10	%

机械性能	额定值	单位制	测试方法
拉伸模量
-- 2	3100	MPa	ASTM D638
--	3100	MPa	ISO 527-2/1
抗张强度
屈服 3	60.0	MPa	ASTM D638
屈服	60.0	MPa	ISO 527-2/5
断裂 3	55.0	MPa	ASTM D638
断裂	55.0	MPa	ISO 527-2/5
伸长率
屈服 3	5.0	%	ASTM D638
屈服	5.0	%	ISO 527-2/5
断裂 3	110	%	ASTM D638
断裂	110	%	ISO 527-2/5

PC+ABS CYCOLOY CE1821 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！ 

简介

ABS工程塑料即PC+ABS（工程塑料合金），在化工业的中文名字叫塑料合金，之所以命名为PC+ABS，是因为这种材料既具有PC树脂的优良耐热耐候性、尺寸稳定性和耐冲击性能，又具有ABS树脂优良的加工流动性。所以应用在薄壁及复杂形状制品，能保持其优异的性能，以及保持塑料与一种酯组成的材料的成型性。ABS工程塑料最大的缺点就是质量重、导热性能欠佳。它的成型温度取于它们两者原料的之间温度，就是240-265度，温度太高ABS会分解，太低PC料的流动性不良。

PC/ABS应用

1.汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件

2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器

3.电信，移动电话外壳，附件以及智能卡（SIM卡）：

4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道

5.家用电器，如洗衣机，吹风机，微波炉内外部件

PC/ABS注塑模工艺条件:

干燥处理：加工前的干燥处理是必须的。湿度应小于0.04%，建议干燥条件为90~110C，2~4小时。

熔化温度： 230~300C。

模具温度：50~100C。

注射压力：取决于塑件。

注射速度：尽可能地高。