LEXAN™ Resin ADX1016R
Technical Datasheet | Supplied by SABIC
LEXAN™ Resin ADX1016R is an amorphous polycarbonate copolymer. Possesses high mechanical, optical, electrical and thermal properties. Exhibits improved chemical resistance, good impact resistance, outstanding dimensional stability and good clarity. Processed by injection molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in3 | ISO 1183 |
| Water Absorption | 0.400 % | 0.400 % | 23°C/sat; ISO 62 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Melt Flow | 8.00 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.00 g/10 min @Load 2.65 lb, Temperature 572 °F |
cm3/10 min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 79.0 % | 79.0 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 7.00 % | 7.00 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.29 GPa | 332 ksi | 1mm/min; ISO 527 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.25 GPa | 326 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 51.0 kJ/m2 | 24.3 ft-lb/in2 | 80*10*3; ISO 180/1A |
| 23.0 kJ/m2 @Temperature -30.0 °C |
10.9 ft-lb/in2 @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 5.00 J/cm2 | 23.8 ft-lb/in2 | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 2.40 J/cm2 @Temperature -30.0 °C |
11.4 ft-lb/in2 @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |