LLDPE EXXONMOBIL LL 1107
| General | |
Availability 1 |
Latin AmericaNorth America |
Additive |
|
Applications |
Blown FilmGarment FilmProduce Bags |
Form(s) |
|
Revision Date |
|
| Resin Properties | Typical Value |
Unit |
Test Based On |
Density |
0.922 |
g/cm3 |
ASTM D1505 |
Melt Index (190°C/2.16 kg) |
0.80 |
g/10 min |
ASTM D1238 |
Peak Melting Temperature |
253 |
°F |
ExxonMobil Method |
| Thermal | Typical Value |
Unit |
Test Based On |
Vicat Softening Temperature |
219 |
°F |
ASTM D1525 |
| Film Properties | Typical Value |
Unit |
Test Based On |
Tensile Strength at Yield MD |
1500 |
psi |
ASTM D882 |
Tensile Strength at Yield TD |
1600 |
psi |
ASTM D882 |
Tensile Strength at Break MD |
8000 |
psi |
ASTM D882 |
Tensile Strength at Break TD |
5000 |
psi |
ASTM D882 |
Elongation at Break MD |
540 |
% |
ASTM D882 |
Elongation at Break TD |
820 |
% |
ASTM D882 |
Secant Modulus MD - 1% Secant |
34000 |
psi |
ASTM D882 |
Secant Modulus TD - 1% Secant |
39000 |
psi |
ASTM D882 |
Dart Drop Impact |
70 |
g |
ASTM D1709A |
Elmendorf Tear Strength MD |
50 |
g |
ASTM D1922 |
Elmendorf Tear Strength TD |
620 |
g |
ASTM D1922 |
Puncture Force |
8 |
lbf |
ExxonMobil Method |
Puncture Energy |
15 |
in·lb |
ExxonMobil Method |
LLDPE EXXONMOBIL LL 1107 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！
注意事项
包装与储运产品装于聚乙烯重包薄膜袋内，外包装为聚丙烯编织袋，每袋净重25kg。贮存仓库应保持清洁、干燥、阴凉和通风良好。可用火车、汽车、轮船、飞机等运输。可按非危险品运输。运输工具应保持清洁、干燥，不得有铁钉等尖锐物。贮运过程中应注意防火、防水、防晒、防尘和防污染等。装卸时不得使用铁钩。
结构特征
被称为第三代聚乙烯的线性低密度聚乙烯(LLDPE)树脂，除具有一般聚烯烃树脂的性能外，其抗张强度、抗撕裂强度、耐环境应力开裂性、耐低温性、耐热性和耐穿刺性尤为优越，获得了注目的发展。
LLDPE虽与过去的LDPE同属于同一密度范围，但由于它们之间的分子结构不同，熔融流变学行为也不同，因此他们的物理基本性质及成型加工特点也不相同。