PEBA PEBAX MH 1657

Polyether block amide PEBAX® MH 1657 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. MH 1657 is an inherently dissipative polymer and can be dry blended or compounded with an isolative polymer to lower the surface resistivity.

Information provided by Arkema Group. Property data for dry samples, unless noted.

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in3	ISO 1183
Water Absorption	120 %	120 %	Sim. to ISO 62
Moisture Absorption	4.50 %	4.50 %	Sim. to ISO 62
Mechanical Properties	Metric	English	Comments
Elongation at Break	>= 50 %	>= 50 %	ISO 527-1/-2
	>= 50 %	>= 50 %	Conditioned; ISO 527-1/-2
Tensile Modulus	0.0800 GPa	11.6 ksi	Conditioned; ISO 527-1/-2
	0.0900 GPa	13.1 ksi	ISO 527-1/-2
50% Modulus	12.0 MPa	12.0 MPa	Conditioned; ISO 527-1/-2
	13.0 MPa	13.0 MPa	ISO 527-1/-2
Flexural Modulus	0.0800 GPa	11.6 ksi	Conditioned 15 days at 23°C - 50% RH; ISO 178
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	Conditioned; ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Conditioned; ISO 179/1eU

PEBA PEBAX MH 1657 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！

PEBA材料是由聚醚和聚酰胺嵌段制备的嵌段共聚物。Deleens发现的四醇盐催化剂族的效率使得超高分子量的材料得以生产，并在1981年以Pebax商标推向市场。它们独特的性能归功于其独特的相分离结构。其中有一个硬质相，主要包括聚酰胺嵌段，以及软质相，主要包括聚醚嵌段。由于这两个嵌段是由酯链接在一起的，所以完整的宏观相分离是可以避免的，目前只有法国阿科玛、瑞士EMS、德国赢创德固赛、日本宇部生产聚酰胺嵌段。

性能

由于独特的化学结构，PEBA材料具备热塑性弹性体里最折衷的性能，包括：

 最轻的工程热塑性弹性体；

 低温下良好和稳定一致的性能；

 反复形变下没有机械性能的损失，并且抗疲劳；

 良好的回弹和弹性恢复；

 精确的尺寸稳定性；以及

 优秀的加工性能。