东莞市恒磊塑胶有限公司
PC LEXAN EXL6013
LEXAN EXL6013 is especially developed for applications requiring a high impact performance combined with an improved chemical resistance over standard polycarbonate.
Information provided by SABIC
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | ISO 1183 |
| Water Absorption | 0.350 % | 0.350 % | 23°C/sat; ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00600 - 0.00800 cm/cm | 0.00600 - 0.00800 in/in | SABIC method |
| Melt Flow | 5.00 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.00 g/10 min @Load 2.65 lb, Temperature 572 °F |
cm3/10 min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | ISO 2039-1 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 7.00 % | 7.00 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1mm/min; ISO 527 |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.15 GPa | 312 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 70.0 kJ/m2 | 33.3 ft-lb/in2 | 80*10*3; ISO 180/1A |
| 60.0 kJ/m2 @Temperature -30.0 °C |
28.6 ft-lb/in2 @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |