东莞市恒磊塑胶有限公司
PET Rynite FG530 NC011
30% Glass Reinforced Polyethylene Terephthalate Developed for Food Contact Applications
Information provided by DuPont. This product line has remained with DuPont after the DuPont-Dow merger.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 162 MPa | 23500 psi | ISO 527-1/-2 |
| Elongation at Break | 2.1 % | 2.1 % | ISO 527-1/-2 |
| Tensile Modulus | 10.5 GPa | 1520 ksi | ISO 527-1/-2 |
| Poissons Ratio | 0.34 | 0.34 | ISO 527-1/-2 |
| Charpy Impact Unnotched | 4.00 J/cm2 @Temperature 23.0 °C |
19.0 ft-lb/in2 @Temperature 73.4 °F |
ISO 179/1eU |
PET Rynite FG530 NC011
成型加工
PET的成型加工可以注塑、挤出、吹塑、涂覆、粘结、机加工、电镀、真空镀金属、印刷。以下主要介绍二种。
1.注塑级①温度设定：射嘴：280~295℃、前段270~275℃、中锻265~275℃、后段250-270℃；螺旋杆转速50~100rpm、模具温度30~85℃、非结晶型之模具为70℃一下、背压5-15KG。②试用除湿干燥机、料管温度240~280℃、射出压力500~1400℃、射出成型温度260~280℃、干燥温度120~140℃、须时2~5小时。
2.薄膜级 先将PET树脂切片预干燥，以防水解，然后在挤出机中于280℃经T形模挤出无定型厚片，经过冷却转鼓或冷却液进行骤冷，使其保持无定形态，以便拉伸定向。厚片再经拉幅机双向拉伸，就成PET薄膜。纵向拉伸就是将厚片预热至86~87℃，并在此温度下沿厚片平面延伸方向拉伸3倍左右，使之取向可以提高结晶度达到较高温度：横向拉伸预热温度98~100℃，拉伸温度100~120℃拉伸比2.5~4.0，热定型温度230~240℃。纵横向拉伸后的薄膜还需经过热定型，以消除由拉伸产生的膜变形，制成热稳定性较好的薄膜。
用途
在塑料分类中，PET的代号是1号，作用广泛：
主要应用为电子电器方面有：电气插座、电子连接器、电饭煲把手、电视偏向轭，端子台，断电器外壳、开关、马达风扇外壳、仪表机械零件、点钞机零件、电熨斗、电磁灶烤炉的配件；汽车工业中的流量控制阀、化油器盖、车窗控制器、脚踏变速器、配电盘罩；机械工业齿轮、叶片、皮带轮、泵零件、另外还有轮椅车体及轮子、灯罩外壳、照明器外壳、排水管接头、拉链、钟表零件、喷雾器部件。
另外：
可纺成聚酯纤维，即涤纶。
可制成薄膜用于录音、录像、电影胶片等的基片、绝缘膜、产品包装等。
作为塑料可吹制成各种瓶，如可乐瓶、矿泉水瓶等。
可作为电器零部件、轴承、齿轮等。